Właściwości kompozycji poli(kwas akrylowy)/modyfikowana skrobia stosowanej jako nowe spoiwo polimerowe

B. Grabowska; B. Pilch-Pitera; K. Kaczmarska; B. Trzebicka; B. Mendrek; D. Drożyński; P. Łątka

doi:10.14314/polimery.2015.179

Published : 2015-03-30

Vol. 60 No. 3 (2015)

Properties of poly(acrylic acid)/modified starch compositions applied as a new polymeric binders

B. Grabowska B. Pilch-Pitera K. Kaczmarska B. Trzebicka B. Mendrek D. Drożyński P. Łątka

DOI: https://doi.org/10.14314/polimery.2015.179

Abstract

The selected physicochemical properties of water-thinnable poly(acrylic acid)/sodiumsalt of carboxymethyl starch (PAA/CMS-Na) compositions — new environmentally friendly polymer binding agents — were investigated as a function of time. The aqueous composition PAA/CMS-Na was stored in closed vessels in a cooling chamber at 10 °C. During the three-month storage period the changes of coloration, viscosity, wetting angle on quartz glass, structure and size distribution of the binding agent particles were studied. On this basis, the stability of the binder properties was preliminarily evaluated. Additionally, the moulding sands containing an aqueous composition PAA/CMS-Naas a binder (stored for a week or three months) were prepared, hardened and subjected to the bending strength tests. It was found, that after three months of storage under conditions resembling those found in a foundry the new binder did not lose its properties as a binding agent for the moulding sand.

Keywords

poli(kwas akrylowy) ; modyfikowana skrobia ; kompozycja polimerowa ; stabilność ; spoiwa odlewnicze poly(acrylic acid) ; modified starch ; polymer composition ; stability ; foundry binders

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Grabowska, B., Pilch-Pitera, B., Kaczmarska, K., Trzebicka, B., Mendrek, B., Drożyński, D., & Łątka, P. (2015). Properties of poly(acrylic acid)/modified starch compositions applied as a new polymeric binders. Polimery, 60(3), 179-185. https://doi.org/10.14314/polimery.2015.179

References

Lewandowski J.L.: „Tworzywa na formy odlewnicze”, WN AKAPIT, Warszawa 1997.

[2] Burian A., Kristek J.: Slevarenstvi 1988, XXXVI (10), 408.

[3] Bortel E.: Environ. Prot. Eng. 1999, 3, 91.

[4] “Fourth report of Institute working group T30”, The Foundryman 1995, 8, 269.

[5] Nicholas K.E.L.: Slevarenstvi 1988, XXXVI (6), 240.

[6] Grabowska B., Holtzer M.: Polimery 2008, 53, 531.

[7] Grabowska B., Holtzer M.: Polimery 2007, 52, 841.

[8] Atanda P.O., Olorunniwo O.E., Alonge. K., Oluwole O.O.: Int. J. Mater. Chem. 2012, 2 (4), 132.

[9] Burian A.: Slevarenstvi 2009, LVII (1—2), 6.

[10] Shehu T., Bhatti R.S.: World Appl. Sci. J. 2012, 16, 858.

[11] Patterson M., Thiel J.: Foundry Manage. Technol. 2010, 6, 14.

[12] Patterson M., Thiel J.: Trans. Am. Foundry Soc. 2011, 119, 331.

[13] Eastman J.: Mod. Cast. 2000, 10, 32.

[14] Eastman J. i in.: Foundry Manag. Technol. 2002, 130, 36.

[15] Zhou X., Jinzong Yang J., Sua D., Qu G.: J. Mater. Proc. Technol. 2009, 209, 5394.
Crossref

[16] Zhou X., Yang J., Qian F., Qu G.: J. Appl. Polym. Sci. 2010, 116, 2893.

[17] Grabowska B., Bulwan M., Zapotoczny Sz., Grabowski G.: Polimery 2012, 57, 529.
Crossref

[18] Grabowska B.: Polimery 2009, 54, 507.

[19] Grabowska B., Holtzer M., Dańko R. i in.: Metalurgija 2013, 52 (1), 47.

[20] Grabowska B., Szucki M., Suchy J.S., Eichholz S., Hodor K.: Polimery 2013, 58, 39.
Crossref

[21] Olejnik E., Janas A., Grabowska B., Kawalec M.: Metalurgija 2012, 51 (4), 406.

[22]
Crossref (data dostêpu 24.03.2014).

[23] Żenkiewicz M.: „Modyfikowanie warstwy wierzchniej tworzyw wielkocząsteczkowych”, WNT, Warszawa 2000.

[24] Vermöhlen K., Lewandowski H., Narres H.D., Koglin E.: Colloids Surf., A 2000, 170, 181.
Crossref

[25] Katalog wybranych materiałów rdzeniowych, formierskich i pomocniczych, Hüttenes Albertus 2011.

Remove [1] Lewandowski J.L.: „Tworzywa na formy odlewnicze”, WN AKAPIT, Warszawa 1997.

[2] Burian A., Kristek J.: Slevarenstvi 1988, XXXVI (10), 408.

[3] Bortel E.: Environ. Prot. Eng. 1999, 3, 91.

[4] “Fourth report of Institute working group T30”, The Foundryman 1995, 8, 269.

[5] Nicholas K.E.L.: Slevarenstvi 1988, XXXVI (6), 240.

[6] Grabowska B., Holtzer M.: Polimery 2008, 53, 531.

[7] Grabowska B., Holtzer M.: Polimery 2007, 52, 841.

[8] Atanda P.O., Olorunniwo O.E., Alonge. K., Oluwole O.O.: Int. J. Mater. Chem. 2012, 2 (4), 132.

[9] Burian A.: Slevarenstvi 2009, LVII (1—2), 6.

[10] Shehu T., Bhatti R.S.: World Appl. Sci. J. 2012, 16, 858.

[11] Patterson M., Thiel J.: Foundry Manage. Technol. 2010, 6, 14.

[12] Patterson M., Thiel J.: Trans. Am. Foundry Soc. 2011, 119, 331.

[13] Eastman J.: Mod. Cast. 2000, 10, 32.

[14] Eastman J. i in.: Foundry Manag. Technol. 2002, 130, 36.

[15] Zhou X., Jinzong Yang J., Sua D., Qu G.: J. Mater. Proc. Technol. 2009, 209, 5394.
Crossref

[16] Zhou X., Yang J., Qian F., Qu G.: J. Appl. Polym. Sci. 2010, 116, 2893.

[17] Grabowska B., Bulwan M., Zapotoczny Sz., Grabowski G.: Polimery 2012, 57, 529.
Crossref

[18] Grabowska B.: Polimery 2009, 54, 507.

[19] Grabowska B., Holtzer M., Dańko R. i in.: Metalurgija 2013, 52 (1), 47.

[20] Grabowska B., Szucki M., Suchy J.S., Eichholz S., Hodor K.: Polimery 2013, 58, 39.
Crossref

[21] Olejnik E., Janas A., Grabowska B., Kawalec M.: Metalurgija 2012, 51 (4), 406.

[22]
Crossref (data dostêpu 24.03.2014).

[23] Żenkiewicz M.: „Modyfikowanie warstwy wierzchniej tworzyw wielkocząsteczkowych”, WNT, Warszawa 2000.

[24] Vermöhlen K., Lewandowski H., Narres H.D., Koglin E.: Colloids Surf., A 2000, 170, 181.
Crossref

[25] Katalog wybranych materiałów rdzeniowych, formierskich i pomocniczych, Hüttenes Albertus 2011.

Google Scholar

Altmetric indicators

Citing articles via

CITEDBY SCOPUS

Statistics

Total abstract views : 126

PDF Downloads : 64

B. Grabowska beata.grabowska@agh.edu.pl

Affiliation
AGH Akademia Górniczo-Hutnicza w Krakowie, Wydział Odlewnictwa, Katedra Inżynierii Procesów Odlewniczych, ul. Reymonta 23, 31-059 Kraków

B. Pilch-Pitera

Affiliation
Politechnika Rzeszowska, Katedra Technologii Tworzyw Sztucznych, Al. Powstańców Warszawy 6, 35-959 Rzeszów

K. Kaczmarska

Affiliation
AGH Akademia Górniczo-Hutnicza w Krakowie, Wydział Odlewnictwa, Katedra Inżynierii Procesów Odlewniczych, ul. Reymonta 23, 31-059 Kraków

B. Trzebicka

Affiliation
Centrum Materiałów Polimerowych i Węglowych, ul. M. Curie-Skłodowskiej 34, 41-819 Zabrze

B. Mendrek

Affiliation
Centrum Materiałów Polimerowych i Węglowych, ul. M. Curie-Skłodowskiej 34, 41-819 Zabrze

D. Drożyński

Affiliation
AGH Akademia Górniczo-Hutnicza w Krakowie, Wydział Odlewnictwa, Katedra Inżynierii Procesów Odlewniczych, ul. Reymonta 23, 31-059 Kraków

P. Łątka

Affiliation
Uniwersytet Jagielloński, Wydział Chemii, Zakład Technologii Chemicznej, ul. Ingardena 3, 30-060 Kraków