Gelation in the non-stoichiometric step growth polymerization of two- and three-functional monomers

Abstract

A random step grow polymerization of two-functional (A2) and three-functional (B3) monomers was studied using a computer simulation method. The focus was on the effect of dividing the process into stages onto the weight-average polymerization degree (Pω) of the resulting polymeric product. It was found that by applying the procedure one can bring to gelation a system that does not form a network when polymerized in a single stage. Such an effect known previously as a result of changes in stoichiometry of a system, can also be observed when the ratio of monomers is the same throughout the whole process. Then, the gelation stems from the growth history of macromolecules.


Details

References

Statistics

Authors

Download files

PDF

Lechowicz, J. (2010). Gelation in the non-stoichiometric step growth polymerization of two- and three-functional monomers. Polimery, 55(7-8), 594–596. Retrieved from https://ichp.vot.pl/index.php/p/article/view/1046