Thixotropic compositions: unsaturated polyester resins/ modified bentonites

M. Oleksy; M. Heneczkowski; H. Galina

Published : 2022-08-26

Vol. 52 No. 5 (2007)

Thixotropic compositions: unsaturated polyester resins/ modified bentonites

M. Oleksy M. Heneczkowski H. Galina

Abstract

Nearly 40 quaternary ammonium chlorides were tested as modifiers of a bentonite (smectic clay). The modified bentonite was used as thixotropic agent for a general purpose unsaturated polyester resin. The modification changed the thermal characteristic of bentonites (DSC) and led to increased distance between layers in bentonite grains (X-ray diffraction). The structure of ammonium salt, namely the kind and size of substituents, had a significant effect on thixotropic properties of unsaturated resin compositions. The thixotropic properties were measured by recording viscosity hysteresis by rotary rheometer and evaluating the absolute and standard thixotropic indices. From the point of view of thixotropic properties of unsaturated polyester compositions, the best quaternary ammonium salt modifier had one benzyl and one slightly branched aliphatic hydrocarbon substituent.

Keywords

nienasycona żywica poliestrowa ; bentonit ; czwartorzędowe sole amoniowe ; właściwości reologiczne ; bezwzględny i standardowy wskaźnik tiksotropii unsaturated polyester resin ; bentonite ; modification quaternary ammonium salts ; rheological properties ; thixotropic indexes ; viscosity hysteresis

Details

References

Statistics

Authors

Download files

PDF

Zasady cytowania

Oleksy, M., Heneczkowski, M., & Galina, H. (2022). Thixotropic compositions: unsaturated polyester resins/ modified bentonites. Polimery, 52(5), 345-350. Retrieved from https://ichp.vot.pl/index.php/p/article/view/1425

References

Kembłowski Z.: “Rheometry of Non-Newtonian Fluids” (in Polish), WNT, Warsaw 1973.

2. Cheng D. C. H., Evans F.: Brit. J. Appl. Phys. 1965, 16, 1599.

3. Cheng D. C. H.: Rheol. Acta 1973, 12, 228.

4. Ferguson J., Hodson N. E.: J. Phys. E. 1975, 8, 526.

5. Hodson N. E., Ferguson J.: Trans. Soc. Rheol. 1976, 20, 265.

6. Kembłowski Z., Petera J.: Rheol. Acta 1979, 18, 702.

7. Kembłowski Z., Petera J.: Rheol. Acta 1980, 19, 529.

8. Pignon F., Magnin A., Piau J. M.: J. Rheol. 1998, 42, 1349.

9. Quemada D.: Eur. Phys. J. Appl. Phys. 1999, 2, 191.

10. O’Brien V. T., Mackay M. E.: J. Rheol. 2002, 46, 557.

11. Bharadwaj R. K., Mehrabi A. R., Hamilton, C., Trujillo C., Murga M., Fan R., Chavira A., Thompson A. K.: Polymer 2002, 43, 3699.

12. Barthelmes G., Pratsinis S. E., Buggisch H.: Chem. Eng. Sci. 2003, 58, 2893.

13. Dullert K., Mewis J.: Rheol. Acta 2005, 45, 23.

14. Jawahar P., Gnanamoorthy R., Balasubramanian M.: Wear 2006, 7--8, 835.

15. Galindo-Rosales F. J., Rubbio-Hernandez F. J.:Appl. Clay Sci. 2006, 33, 109.

16. Mao C. F., Chen J. C.: Food Hydrcoll. 2006, 20, 730.

17. Brzozowska T., Zieliński J.: Polimery 2006, 51, 212.

18. Oleksy M.: “Thixotropic compositions of unsaturated polyester resins of improved stability with modified smectites” (in Polish), PhD Thesis, 2000, Silesian University of Technology, Gliwice.

19. Oleksy M., Galina H.: Polimery 1999, 44, 430.

20. Oleksy M., Galina H.: Polimery 2000, 45, 541.

21. Galina H., Oleksy M.: in “Quaternary ammonium salts and their applications” (in Polish), Wyd. Inst. Techn. Drewna, Poznań 2001, str. 133--146.

22. Oleksy M., Heneczkowski M.: Polimery 2004, 49, 806.

23. Oleksy M., Heneczkowski M.: Polimery 2005, 50, 143.

24. Oleksy M., Heneczkowski M., Galina H.: Polimery 2006, 51, 799.

25. Polish Pat. PL 178 899 (2000).

26. Polish Pat. PL 178 900 (2000).

27. Pigłowski J., Kiersnowski A., Dołęga J.: Polimery 2006, 51, 704.

28. Gołębiewski J., Różański A., Gałęski A.: Polimery 2006, 51, 374.

Google Scholar

Altmetric indicators

Citing articles via

Statistics

Total abstract views : 158

PDF Downloads : 27

M. Oleksy molek@prz.edu.pl

Affiliation
Rzeszow University of Technology, Faculty of Chemistry, 35-959 Rzeszow, Poland

M. Heneczkowski

H. Galina