Nanokompozyty polipropylenu i polietylenu z glinkami typu montmorylonit

A. Pawlak; J. Morawiec; E. Piorkowska; A. Galeski

Published : 2022-09-01

Vol. 49 No. 4 (2004)

Nanocomposites of polypropylene and polyethylene with montmorillonite type clays

A. Pawlak J. Morawiec E. Piorkowska A. Galeski

Abstract

General characteristics of polymeric nanocomposites containing montmorillonite (MMT) as well as the results of research concerning preparation and properties of nanocomposites with this filler, based on isotactic polypropylene (i-PP) or low density polyethylene (PE-LD) were presented. Structure, crystallization and mechanical properties of the nanocomposites were studied using X-ray diffraction, transmission electron microscopy, scanning electron microscopy, light microscopy, differential scanning calorimetry and tensile test. Blending conditions as well as type of a compatibilizer used (polypropylene grafted onto maleic anhydride or acrylic acid) significantly influence MMT exfoliation in i-PP matrix. MMT presence weakly influences i-PP crystallization at static conditions while causes intense spherulites nucleation under shear. Dependencies of tensile properties of nanocomposites based on i-PP matrix on MMT content and exfoliation degree (Figs 1-2) were investigated and interpreted. Polypropylene based nanocomposites exhibit increased elastic modulus while preserving accepted value of the elongation at break. Nanocomposites based on low density polyethylene exhibit high ability to plastic deformation. Films of compatibilized polyethylene nanocomposites were obtained using blow moulding technique and the effects of stretch and blowing degree on mechanical properties of the films (Table 1) were investigated.

Keywords

nanokompozyty ; polipropylen ; polietylen małej gęstości ; kompatybilizatory ; montmorylonit ; rozwarstwianie montmorylonitu ; krystalizacja nanocomposites ; polypropylene ; low-density polyethylene ; compatibilizers ; montmorillonite ; exfoliation ; crystallization

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Pawlak, A., Morawiec, J., Piorkowska, E., & Galeski, A. (2022). Nanocomposites of polypropylene and polyethylene with montmorillonite type clays. Polimery, 49(4), 240-247. Retrieved from https://ichp.vot.pl/index.php/p/article/view/1746

References

Otaigbe J. U., Barnes M. D., Fukui K., Sumpter B. G., Noid D. W.: Adv. Polym. Sci. 2001,154,1.

2. Cased W.: Macromol. Rapid Commun. 2000, 21.705.

3. Giannelis E. P.: Adv. Mat. 1996,8,29.

4. Biswas M., Sinha R. S.: Adv. Polym. Sci. 2001,155,167.

5. Manias E., Touny A., Wu L., Strawhecker K., Lu B., Chung T. C.: Chem. Mater. 2001,13,3516.

6. Hasegawa N„ Okamoto H., Kato M., Tsukigase A.: Macromol. Mater. Eng. 2000,280. 76.

7. Kawasumi M., Hasegawa W, Kato M., Usuki A., Okada A.: Macromolecules 1997, 30,6333.

8. Maiti P., Nam P. H., Okamoto M., Hasegawa N„ Usuki A.: Macromolecules 2002,35,2042.

9. Svoboda P„ Zeng Ch., Wang H., Lee Tomasko D. L.: I. Appl. Polym. Sci. 2002,85,1562.

10. Xu W., Ge M„ He P.: J. Polym. Sci.. Part B: Polym. Phys. 2002,40,408.

11. Ma J„ Zhang S., Qi Z., Li G., Hu Y: J. Appl. Polym. Sci. 2002,83, 1978.

12. Pozsgay A., Frater T„ Papp L., Sajo 1., Pukanszky B.: J. Macrom. Sci., Part B-Physics 2002, B41,1249.

13. Oya A., Kurokawa Y, Yasuda H.: I. Mater. Sci. 2000, 35,1045.

14. Jin Y. H„ Park H. )., Im S. S., Kwak S. Y, Kwak S.: Macromol. Rapid. Comm. 2002, 23,135.

15. Alexandre M., Dubois P., SunT., Garces J. M., Jerome R.: Polymer 2002,43, 2123.

16. Heineman J„ Reichtert P., Thomann R., Mulhaupt R.: Macromol. Rapid. Comm. 1999, 20, 423.

17. Song L., Wang S. F., Chen Z, Y, Fan W. C: J. Mater. Chem. 2002,12,3152.

18. Wang K. H., Choi M. H., Koo Ch. M., Choi Y. S., Chung I. J.: Polymer 2001,42,9819

19. GopakumarT. G., LeeJ. A., Kontonopulu M., Parent J. S.: Polymer 2002,43,5483.

20. Wang K. H., Choi M. H„ Koo Ch. M„ Chung 1. J., Jang M. Ch., Choi S. W., Song H. H.: J. Polym Sci.. Part B: Polym. Phys. 2002,40,1454.

21. Morawiec J„ Pawlak A„ Slouf M., Galeski A., Piorkowska E.: Polimery 2004,49,52.

22. Pawlak A., Morawiec J., Galeski A., Piórkowska E.: dane nieopubiikowane.

23. Pawlak A., Morawiec J., Piórkowska E., Galeski A.: Solid State Phenom. 2003,94, 335.

24. Ślusarski L., Bieliński D., Głąb P„ Pawlak A., Morawiec J., Galeski A., Piórkowska F..: Archiwum Nauki o Materiałach (w druku).

25. Nowacki R., Monasse B., Piórkowska E., Galeski A., Haudin J. M.: Polymer (wysłane do druku).

26. Morawiec ]., Pawlak A., Galeski A., Piórkowska E„ Krasnikowa N.: dane nieopublikowane.

27. Morawiec J,, Pawlak A., Galeski A., Piorkowska E.: dane nieopubiikowane.

Remove 1. Otaigbe J. U., Barnes M. D., Fukui K., Sumpter B. G., Noid D. W.: Adv. Polym. Sci. 2001,154,1.

2. Cased W.: Macromol. Rapid Commun. 2000, 21.705.

3. Giannelis E. P.: Adv. Mat. 1996,8,29.

4. Biswas M., Sinha R. S.: Adv. Polym. Sci. 2001,155,167.

5. Manias E., Touny A., Wu L., Strawhecker K., Lu B., Chung T. C.: Chem. Mater. 2001,13,3516.

6. Hasegawa N„ Okamoto H., Kato M., Tsukigase A.: Macromol. Mater. Eng. 2000,280. 76.

7. Kawasumi M., Hasegawa W, Kato M., Usuki A., Okada A.: Macromolecules 1997, 30,6333.

8. Maiti P., Nam P. H., Okamoto M., Hasegawa N„ Usuki A.: Macromolecules 2002,35,2042.

9. Svoboda P„ Zeng Ch., Wang H., Lee Tomasko D. L.: I. Appl. Polym. Sci. 2002,85,1562.

10. Xu W., Ge M„ He P.: J. Polym. Sci.. Part B: Polym. Phys. 2002,40,408.

11. Ma J„ Zhang S., Qi Z., Li G., Hu Y: J. Appl. Polym. Sci. 2002,83, 1978.

12. Pozsgay A., Frater T„ Papp L., Sajo 1., Pukanszky B.: J. Macrom. Sci., Part B-Physics 2002, B41,1249.

13. Oya A., Kurokawa Y, Yasuda H.: I. Mater. Sci. 2000, 35,1045.

14. Jin Y. H„ Park H. )., Im S. S., Kwak S. Y, Kwak S.: Macromol. Rapid. Comm. 2002, 23,135.

15. Alexandre M., Dubois P., SunT., Garces J. M., Jerome R.: Polymer 2002,43, 2123.

16. Heineman J„ Reichtert P., Thomann R., Mulhaupt R.: Macromol. Rapid. Comm. 1999, 20, 423.

17. Song L., Wang S. F., Chen Z, Y, Fan W. C: J. Mater. Chem. 2002,12,3152.

18. Wang K. H., Choi M. H., Koo Ch. M., Choi Y. S., Chung I. J.: Polymer 2001,42,9819

19. GopakumarT. G., LeeJ. A., Kontonopulu M., Parent J. S.: Polymer 2002,43,5483.

20. Wang K. H., Choi M. H„ Koo Ch. M„ Chung 1. J., Jang M. Ch., Choi S. W., Song H. H.: J. Polym Sci.. Part B: Polym. Phys. 2002,40,1454.

21. Morawiec J„ Pawlak A„ Slouf M., Galeski A., Piorkowska E.: Polimery 2004,49,52.

22. Pawlak A., Morawiec J., Galeski A., Piórkowska E.: dane nieopubiikowane.

23. Pawlak A., Morawiec J., Piórkowska E., Galeski A.: Solid State Phenom. 2003,94, 335.

24. Ślusarski L., Bieliński D., Głąb P„ Pawlak A., Morawiec J., Galeski A., Piórkowska F..: Archiwum Nauki o Materiałach (w druku).

25. Nowacki R., Monasse B., Piórkowska E., Galeski A., Haudin J. M.: Polymer (wysłane do druku).

26. Morawiec ]., Pawlak A., Galeski A., Piórkowska E„ Krasnikowa N.: dane nieopublikowane.

27. Morawiec J,, Pawlak A., Galeski A., Piorkowska E.: dane nieopubiikowane.

Google Scholar

Citing articles via

Statistics

Total abstract views : 43

PDF Downloads : 47

A. Pawlak polimery@ichp.pl

Affiliation
Centrum Badań Molekularnych i Makromolekularnych, Polska Akademia Nauk, uI. Sienkiewicza 112, 90-363 Łódź

J. Morawiec

Affiliation
Centrum Badań Molekularnych i Makromolekularnych, Polska Akademia Nauk, uI. Sienkiewicza 112, 90-363 Łódź

E. Piorkowska

Affiliation
Centrum Badań Molekularnych i Makromolekularnych, Polska Akademia Nauk, uI. Sienkiewicza 112, 90-363 Łódź

A. Galeski

Affiliation
Centrum Badań Molekularnych i Makromolekularnych, Polska Akademia Nauk, uI. Sienkiewicza 112, 90-363 Łódź