Jonomery poliuretanowe. Cz. I. Otrzymywanie, struktura, właściwości i zastosowanie anionowych dyspersji poliuretanowych i poliuretanowo-akryIowych

P. Król; B. Król

Published : 2022-09-01

Vol. 49 No. 7-8 (2004)

Polyurethane ionomers. Part I. Preparation, structure, properties and application of anionic polyurethane or polyurethane-acrylic dispersions

P. Król B. Król

Abstract

Several polyurethane anionomers have been synthesized (Table 1) in the reactions of toluilene (TDI) or isophorone diisocyanatcs, polyester or polyether polyols and dihydroxyacids. Urethane - isocyanate prepolymers have been extended with 1,6-hexamethyldiamine or terminated with 2-hydroxyethyl acrylate. They were eventually then copolymerized, in emulsion, with other acrylic monomers in the presence of free radical initiators (Table 2 and 3). 1H NMR or IR spectra confirm the expected structures of PUR anionomers and introduction of polar ionic groups (Figs. 1-3). GPC investigations showed that besides oligourethane anionomers also the components showing much higher molecular weights were present (Figs. 4 and 5) what influenced the viscosity or surface tension of aqueous dispersions prepared. The following properties of the products obtained in a form of coatings were investigated: dry substance content, hardness after seasoning, abrasion, flexibility, impact strength and gloss (Figs. 6-10). The investigations done allowed to choose the dispersion based on TDI and oligo(oxylenecaprolactone)diol as the best one to produce the varnish coatings.

Keywords

jonomery poliuretanowe ; makroanionomery uretanowo-akrylowe ; wodne dyspersje lakiernicze ; kąt zwilżania ; właściwości użytkowe polyurethane ionomers ; varnish coatings ; polyurethanes ; polyacrylates ; contact angle ; rheological properties

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Król, P., & Król, B. (2022). Polyurethane ionomers. Part I. Preparation, structure, properties and application of anionic polyurethane or polyurethane-acrylic dispersions. Polimery, 49(7-8), 530-540. Retrieved from https://ichp.vot.pl/index.php/p/article/view/1781

References

Santere J. P., Brash J. L.: Ind. Eng. Chem. Res. 1997,36, 1352.

2. Melchirs M., Sonntag M., Kobusch c., Jurgens E.: Prago Org. Coat. 2000,40,99.

3. Ad E.: Verkroniek 2000, 73, 31.

4. Robila G., Burulana T., Burulana E. c. Eur. Polym. J. 1999,35,1305.

5. Pat. USA 5 610 232 (1994).

6. Pat. USA 6191214 (2001).

7. Sang Yup L., Jeong Sam L., Byung Kyu K: Polym. Int. 1997,42,67.

8. Harjunalanem T., Lathtinen M.: Eur. Polym. Sci. 2003, 39,817.

9. Pat. WO O 259158 (2001).

10. Wu K L., Mc Anany W. J.: Amer. Ceram. Soc. Bull. 1995,74,61.

11. Kumar D. B., Reddy M. R, Mulay V. N., Krishnamurti N.: Eur. Polym. J. 2000,36,1503.

12. Pat. jap. 351 805 (2000).

13. Pat. niem. 1 020195 (2001).

14. Pat. jap. 302713 (2001).

15. Pat. Eur. 1 164151 (2001).

16. Pat. niem. 19949971 (2001).

17. Pat. bryt. 2369122 (2000).

18. Vendenoorde P., Van de Watewring P.: Pint Acabados Ind. 2000,24,27.

19. Pat. niem. 10112365 (2001).

20. Zinnermann J., Sunder A., Mulhaupt R: J. Palym. Sci., Part A, Polym. Chem. 2002,40,2085.

21. Lee K H., Kim B. K: Polymer 1996, 37, 2251.

22. Pat. jap. 2001 055479; C.A. 134 180 034f.

23. Maquanint K, Sanderson R: Polymer 2003, 44, 2631.

24. Pat. niem. 19924415 (2000). 134,30 438b.

25. Hong Tao Z., Rong G., Zhao Hui Y., Liu Lan L.:]. Appl. Polym. Sci. 2001,82,941.

26. Barbeau Ph., Gerard J. F., Magny B., Pascault J. P: J. Polym. Sci., Part B, Polym. Phys. 2000,38,2750.

27. Król P., Król B., Pielichowski J., Potoczek M.: Ma ter. Ceram. 2002,4, 129.

28. Pol. zglosz. pat. C08F 212/00, Biul. Urz. Pat. 2001, 20(724), s. 26.

29. Potoczek M., Heneczkowski M., Oleksy M.: Ceram. Int. 2003,29,259.

30. Young-Kuk J., In-Wood Ch., Jung-Hyun K: Collaid Surface. Physicochem. Eng. Aspect. 2001, 179, 71.

31. Manock H. L.: Pigment Resin Technology 2000, 29, 3.

32. Oertel G.: "Polyurethane Handbook", 2 ed., Hanser Publisher, Nowy Jork 1994, str. 27.

33. Hirose M., Zhou J., Nagai K: Prago Org. Coat. 2000, 38,27.

34. Cloutet E., Radharkrishman B., Cramail H.: Polym. Inter. 2002, 51, 978.

35. Kukanja D., Krajnc M.: Materiali in Technologije 2002, 36,81.

36. Spychaj T., Spychaj s.: "Farby i kleje wodorozcieńczalne", WNT, Warszawa 1996.

37. Pat. jap. 265525 (2002).

38. Stagg F. E.: Analyst 1966,71,557.

39. PN-84/C-81512.

40. PN-92/C-89402.

41. Żenkiewicz M.: "Adhezja i modyfikowanie warstwy wierzchniej tworzyw sztucznych", WNT, Warszawa 2000.

42. PN-79/C-81530.

43. PN-76/C-81516.

44. PN-76/C-81528.

45. PN-54/C-81526.

46. PN-81/C-81550.

47. Katalog firmy ZENECA-Resins (Holandia) dotyczący żywic typu NeoRez (2002).

33. Hirose M., Zhou J., Nagai K: Prago Org. Coat. 2000, 38,27.

34. Cloutet E., Radharkrishman B., Cramail H.: Polym. Inter. 2002, 51, 978.

35. Kukanja D., Krajnc M.: Materiali in Technologije 2002, 36,81.

36. Spychaj T., Spychaj s.: "Farby i kleje wodorozcieńczalne", WNT, Warszawa 1996.

37. Pat. jap. 265525 (2002).

38. Stagg F. E.: Analyst 1966,71,557.

39. PN-84/C-81512.

40. PN-92/C-89402.

41. Żenkiewicz M.: "Adhezja i modyfikowanie warstwy wierzchniej tworzyw sztucznych", WNT, Warszawa 2000.

42. PN-79/C-81530.

43. PN-76/C-81516.

44. PN-76/C-81528.

45. PN-54/C-81526.

46. PN-81/C-81550.

47. Katalog firmy ZENECA-Resins (Holandia) dotyczący żywic typu NeoRez (2002).

">Google Scholar

Citing articles via

Statistics

Total abstract views : 87

PDF Downloads : 167

P. Król polimery@ichp.pl

Affiliation
Politechnika Rzeszowska, Zakład Technologii Tworzyw Sztucznych, ul. Powstańców Warszawy 6, 35-959 Rzeszów

B. Król

Affiliation
Politechnika Rzeszowska, Zakład Technologii Tworzyw Sztucznych, ul. Powstańców Warszawy 6, 35-959 Rzeszów