Dispersion polymerization of dilactide and epsilon-caprolactone
Abstract
Ring-opening polymerization of dilactide and epsilon- caprolactone carried on in 1,4-dioxane - heptane mixed solvent in the presence of poly(dodecyl acrylate)-g-poly(epsilon- caprolactone) surface active agent led to formation of polyesters shaped into microspheres with diameters from 0.6 to 7.4 mum and with small diameter polydispersity factor ((D) over bar (w)/(D) over bar (n)). Studies of the mechanism of particle formation revealed that all growing chains became incorporated into microspheres at the very beginning, when monomer conversion was low (less than or equal to10%) and that the number of the initially formed microspheres did not change with time. Thus, subsequent monomer additions resulted in increasing volumes of particles without affecting their number in suspension. It has been found also that in the polymerization of dilactide the average number of propagating macromolecules per microsphere was independent from the initial initiator concentration and the increased initiator concentration resulted in increased number of particles. This observation conformed to the model illustrating formation and growth of microspheres according to which new particles are formed by collision of two polyester chains with molecular weight exceeding the critical ones and subsequently other chains are ncorporated into existing particles by accretion. Thus, by election of the required initial initiator and total monomer concentration (introduced in one or in more steps to the polymerizing mixture) it was possible tailoring of particle concentration and particle diameters.
Details
Statistics
Authors
Zasady cytowania
Słomkowski, S., Sosnowski, S., & Gadzinowski, M. (2022). Dispersion polymerization of dilactide and epsilon-caprolactone. Polimery, 47(7-8), 485–490. Retrieved from https://ichp.vot.pl/index.php/p/article/view/1991