Modyfikacja polimerów za pomocą bombardowania jonowego. Cz. II. Modyfikacja funkcjonalnych właściwości gumy

U. Ostaszewska; D. Pieczyńska; D. M. Bieliński; J. Jagielski

Published : 2012-02-28

Vol. 57 No. 2 (2012)

Modification of polymers with the application of ion beam bombardment. Part II. Modification of functional properties of rubber

U. Ostaszewska D. Pieczyńska D. M. Bieliński J. Jagielski

Abstract

The surface of rubbers: natural (NR), styrene-butadiene (SBR) and acrylonitrile-butadiene (NBR) or its mixes with chloroprene rubber (NBR/CR) were subjected to high-energy He+, O+, Ar+ or F+ ion beam treatment. Based on the changes in the chemical composition and physical structure of rubber macromolecules in the surface layer and on the surface geometry of ion-irradiated materials, the effect of this modification on the functional properties of the vulcanizates was evaluated. Interactions between high energy ion beam and macromolecules are of elastic character (resulting in an ionization with release of hydrogen — Fig. 1), or inelastic, leading to the degradation of polymer. Graphitization, together with an increased degree of crosslinking of the surface layer, result in an increase in the microhardness of the rubber subjected to ion bombardment (Fig. 2). The shrinkage associated with higher crosslinking of the material causes the formation of a microcrack network on the vulcanizate surface (Fig. 3). The oxidation (Table 2) and the increased surface roughness, change the wettability of rubber surface (Fig. 7) and the friction (Fig. 4), while the polarization and surface development increase the adhesion (Table 3) and bacteriostaticity (Table 6) of the modified vulcanizates. The rubber surface layer subjected to ion bombardment can play a role of a protective barrier, which prevents the inside of material from the action of various chemical or biological factors. As a result of the modification, the rubber becomes more resistant to ageing (both thermal and ozone — Fig. 9), exhibits improved thermal stability (Table 4) and reduced flammability (Table 5) as well as the increased resistance to fuel (Fig. 10) and bacteria.

Keywords

guma ; bombardowanie jonowe ; warstwa wierzchnia ; modyfikacja rubber ; ion bombardment ; surface layer ; modification

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Ostaszewska, U., Pieczyńska, D., Bieliński, D. M., & Jagielski, J. (2012). Modification of polymers with the application of ion beam bombardment. Part II. Modification of functional properties of rubber. Polimery, 57(2), 124–134. Retrieved from https://ichp.vot.pl/index.php/p/article/view/814

References

Bieliński D. M., Jagielski J., Lipiński P., Pieczyńska D., Ostaszewska U., Piątkowska A.: Am. Inst. Phys.: Conf. Proc. Ser. 2009, 1099, 357.

2. Lee E. H.: Nucl. Instr. Meth. 1999, B 151, 29.

3. Dong H., Bell T.: Surf. Coat. Technol. 1999, 111, 29.

4. Abdul-Kader A. M., Turos A., Grambole D., Jagielski J., Piątkowska A., Madi, N. K. Al-Maadeed M.: Nucl. Instr. Meth. 2005, B 240, 152.

5. Abdul-Kader A. M., Turos A., Jagielski J., Nowicki L., Ratajczak R., Stonert A., Al-Maadeed M.: Vacuum 2005, 78, 281.

6. Bieliński D. M., Tranchida D., Lipiński P., Jagielski J., Turos A.: Vacuum 2007, 81, 1256.

7. Jagielski J., Turos A., Abdul-Kader A. M., Piątkowska A., Bieliński D. M.: Nucl. Instr. Meth. 2007, B 261, 690.

8. Park J. W., Sohn C. W., Choi B. H.: Curr. Appl. Phys. 2006, 6, 188.

9. Jagielski J., Grambole D., Jóźwik I., Bieliński D. M., Ostaszewska U., Pieczyńska D.: Mater. Chem. Phys. 2011, 127, 342.

10. www.micromaterials.com

11. Bieliński D. M.: Kautsch. Gummi Kunstst. 2009, 62, 50.

12. Pieczyńska D., Ostaszewska U., Bieliński D. M., Jagielski J.: Polimery 2011, 56, 13.

13. Bieliński D. M., Ślusarski L., Affrossman S., Pethrick R. A.: Kautsch. Gummi Kunstst. 1998, 51, 429.

14. Bieliński D. M., Ślusarski L., Kleps T., Parasiewicz W.: Prog. Rubber Plast. Technol. 1999, 15, 123.

15. Ślusarski L., Zaborski M.: w "Advances in Polymer Blends and Alloys Technology" (red. Finlayson K.), Technomic Publishing Co., Lancaster (UK) 1993, t. IV, s. 163.

16. Ślusarski L., Zaborski M.: w "Polymer Blends Processing, Morphology and Properties", Plenum Press, New York -- London 1984, t. II, s. 143.

17. Anachkov M. P., Stefanova R. V., Rakovsky S. K.: J. Appl. Polym. Sci. 1989, 21, 429.

18. Ziegler J. F., Biersack J. P., Littmark U.: "The Stopping and Ranges of Ions in Solids", Pergamon Press, New York 1985, vol. 1.

19. Zgłosz. pat. P-383 453 (2007).

20. Bieliński D. M., Jagielski J., Pankiewicz D.: Gummi Fasern Kunstst. 2009, 62, 201.

21. Moore D.: "Friction and Lubrication of Elastomers", Pergamon Press, Oxford -- New York -- Toronto -- Sydney -- Braunschweig 1972.

22. Bowden F. P., Tabor D.: "Friction. An Introduction to Tribology", Anchor Press, Doubleday Garden City -- New York 1973.

23. Bieliński D. M.: "Tribologia elastomerów i gumy z perspektywy inżynierii materiałowej", Wyd. Naukowe Instytutu Technologii Eksploatacji -- PIB, Radom 2009.

24. Harrick N. J.: "Internal Reflectance Spectroscopy", Wiley -- Interscience, New York 1967.

25. Garbassi F., Morra M. Occhiello E.: "Polymer Surfaces. From Physics to Technology", John Wiley & Sons, Chichester -- New York -- Weinheim -- Brisbane -- Singapore -- Toronto 1998.

26. Borutto A., Crivellone C., Marani F.: Wear 1998, 222, 57.

27. Zgłosz. pat. P-392 815 (2010).

28. Smith L. P.: "The Language of Rubber", Butterworth -- Heinemann, Oxford 1993.

29. Lipiński P., Bieliński D. M., Okrój W., Jakubowski W., Klimek L., Jagielski J.: Vacuum 2009, 83, S200.

30. Carlson J. D., Bares J. E., Guzman A. M., Pronko P. P.: Nucl. Instr. Meth. 1985, B 7/8, 507.

Google Scholar

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0

U. Ostaszewska polimery@ichp.pl

D. Pieczyńska

D. M. Bieliński

J. Jagielski