Właściwości kompozytów polimerowych z udziałem proszków lub płatków miedzi jako napełniaczy

P. Łoś; A. Łukomska; S. Kowalska; R. Jeziórska; J. Krupka

Published : 2012-05-30

Vol. 57 No. 5 (2012)

Properties of polymer composites with copper powders or flakes as fillers

P. Łoś A. Łukomska S. Kowalska R. Jeziórska J. Krupka

Abstract

In this paper mechanical and electromagnetic properties as well as the structure of polymer composites based on several polymer matrices, [(ethylene-vinyl acetate (EVA), low-density polyethylene (PE-LD), linear low density polyethylene (PE-LLD), polypropylene (PP) and hard polyvinyl chloride (PVC)], filled with copper powders or flakes are presented. The studied materials were formed by extrusion of small beads of polymer mixed with the copper powders/flakes. The copper filler concentration ranged from 0.1 to 40 wt. %. The copper powders and flakes were obtained by potentiostatic or galvanostatic pulse electrolysis from industrial wastewaters as well as copper sulfate electrolytes. The control of the size and shape of copper flakes and powders was achieved by the application of appropriate time and values of current or potential pulse, respectively. The results of electromagnetic measurements performed using split post dielectric resonator method indicated that studied materials exhibit smaller than unity the effective magnetic permeability and relatively high effective permittivity, which is typical for metamaterials composed of dielectric and a metal. Also, for several polymer composites the correlations between selected mechanical and dielectric properties were found. Multilayered polymer composites with different filler content in particular layers were also studied. In this case the best measure of effectiveness of electromagnetic shielding is described by the quality factor. On the basis of the obtained data it was stated that materials made of two layers of polymer composites are the most promising in EMI applications.

Keywords

kompozyty polimerowe ; nanomiedź ; ekranowanie pola elektromagnetycznego ; metamateriały polymer composites ; nanocopper ; electromagnetic interference shielding ; metamaterials

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Łoś, P., Łukomska, A., Kowalska, S., Jeziórska, R., & Krupka, J. (2012). Properties of polymer composites with copper powders or flakes as fillers. Polimery, 57(5), 338-346. Retrieved from https://ichp.vot.pl/index.php/p/article/view/832

References

Hoffman A. J., Alekseyev L., Howard S. S, Franz K. J., Wasserman D., Podolskiy V. A., Narimanov E. E., Sivco D. L., Gmachl C.: Nature Mater. 2007, 6, 946.

2. KoledintsevaM. Y., Drewniak J., DuBro R.: Prog. Electromagnet. Res. B 2009, 15, 197.

3. Liu Z., Bai G., Huang Y., Ma Y., Du F., Li F., Guo T., Chen Y.: Carbon 2007, 45, 821.

4. Wong K. H., Pickering S. J., Rudd C. D.: Composites Part A: Appl. Sci. Manuf. 2010, 41 (6), 693.

5. Gelves G. A., Lin B., Sundararaj U., Haber J. A.: Nanotechnology 2008, 19, 215 712.

6. Chung D. D. L.: Carbon 2001, 39, 279.

7. Pat. PCT/PL 000 022 (2010).

8. £ukomska A., Plewka A., Łoś P.: J. Electroanal. Chem. 2009, 633, 92.

9. £ukomska A., Plewka A., £oś P.: J. Electroanal. Chem. 2009, 637, 50.

10. Zgłosz. pat. P 3922 82 (2010).

11. £oś P., £ukomska A., Kowalska S., Jeziórska R., Krupka J.: Polimery 2011, 56, 324.

12. £oś P., £ukomska A., Kowalska S., Jeziórska R., Zaprzalski P., Krupka J.: Mater. Sci. Poland 2011, 29 (1), 35.

13. Wang L. L., Tay B. K., See K. K., Sun Z., Tan L. K., Lua D.: Carbon 2009, 47, 1905.

14. Krupka J., Derzakowski K., Hartnett J. G.: Meas. Sci. Technol. 2009, 20, 105 702.

15. Pande S., Singh B. P., Mathur R. B., Dhami T. L., Saini P., Dhawan S. K.: Nanoscale Res. Lett. 2009, 4, 327.

Google Scholar

Citing articles via

Statistics

Total abstract views : 90

PDF Downloads : 100

P. Łoś polimery@ichp.pl

A. Łukomska

S. Kowalska

R. Jeziórska

J. Krupka