Wpływ nanonapełniacza polimerowego o budowie „rdzeń-otoczka” na strukturę oraz właściwości mieszaniny polilaktydu i termoplastycznej skrobi kukurydzianej

R. Jeziórska; A. Szadkowska; B. Świerz-Motysia; J. Kozakiewicz

Published : 2012-05-30

Vol. 57 No. 5 (2012)

Effect of "core-shell” polymeric nanofiller on the structure and properties of polylactide and thermoplastic corn starch blend

R. Jeziórska A. Szadkowska B. Świerz-Motysia J. Kozakiewicz

Abstract

The influence of "core-shell” polymeric nanofiller (DASI) and compatibilizer (maleated polylactide —MPLA) on the structure, mechanical and barrier properties of polylactide and thermoplastic starch blend was investigated. All materials were compounded in a co-rotating twin-screw extruder and then injection molded. The composites were characterized with SEM (Figs. 1—3), DSC (Fig. 4) and DMTA (Fig. 5) methods. Tensile and flexural mechanical and barrier properties were also determined. The addition of DASI in the presence of maleated PLA improves adhesion between the PLA and TPS. It was found out, that contents of DASI particles have great impact on nanocomposites properties. Melting temperature and crystallinity were found to decrease by adding TPS as well as DASI (Table 1). PLA/MPLA/TPS/DASI nanocomoposites showed significantly lower stiffness due to lower storage modulus than pure PLA. However, G' slightly increases as a function of nanofiller (Table 2). Moreover, dynamic mechanical thermal analysis demonstrated that relaxation temperatures (Ta, Tb, Tg) of PLA/MPLA/TPS/DASI nanocomposites decreased (Tables 3, 4). The gradual enhancement in impact, tensile and flexural strengths of PLA/TPS blend containing MPLA was observed (Table 5). The addition of DASI nanoparticles to the PLA/MPLA/TPS blend increased impact strength and elongation at break and decreased tensile and flexural modulus simultaneously (Table 6). The improved barrier properties of nanocomposites containing TPS can also be mentioned as a positive effect (Table 7).

Keywords

nanokompozyty ; polilaktyd ; termoplastyczna skrobia ; nanonapełniacz o budowie „rdzeń-otoczka” nanocomposites ; polylactide ; thermoplastic starch ; "core-shell” nanofiller

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Jeziórska, R., Szadkowska, A., Świerz-Motysia, B., & Kozakiewicz, J. (2012). Effect of "core-shell” polymeric nanofiller on the structure and properties of polylactide and thermoplastic corn starch blend. Polimery, 57(5), 354–363. Retrieved from https://ichp.vot.pl/index.php/p/article/view/834

References

Duda A.: Przem. Chem. 2003, 82, 905.

2. Ju L., Dean K. i in.: Prog. Polym. Sci. 2006, 31, 56.

3. Ray S. S., Okamoto M.: Prog. Polym. Sci. 2003, 28, 1539.

4. Ray S. S., Bousmina M.: Prog. Mater. Sci. 2005, 50, 962.

5. Świerz-Motysia B., Jeziórska R., Szadkowska A., Piotrowska M.: Polimery 2011, 56, 271.

6. Pluta M.: Polymer 2004, 45, 8239.

7. Ray S. S., Yamada K. i in.: Polymer 2003, 44, 6633.

8. Nam J. Y, Ray S. S., Okamoto M.: Macromolecules 2003, 36, 7126.

9. Solarski S., Ferreira M, Devaux E.: Polym. Degrad. Stab. 2008, 93, 707.

10. Żenkiewicz M., Richert J.: Przem. Chem. 2008, 87, 864.

11. Fukushima K., Abbate C. i in.: Polym. Degrad. Stab. 2009, 94, 1646.

12. Wu C. S., Liao H. T.: Polymer 2007, 48, 4449.

13. Song W., Zheng Z. i in.: Polymer 2007, 48, 3658.

14. Kuan C-F., Kuan H-C. i in.: J. Phys. Chem.Solid. 2008, 69, (1), 1395.

15. Xu X. L., Chen X. S. i in.: Eur. Polym J. 2007, 43, 3187.

16. Petersson L., Oksman K.: Compos. Sci. Technol. 2006,66, 2187.

17. Ray S. S.,Yamada K. i in.: Polymer 2003, 44, 857.

18. Krikorian V., Pochan D.: Macromolecules 2004, 37, 6480.

19. Tallin C., Orroyh C. i in.: Polymer 2005, 46, 11716.

20. Żenkiewicz M., Richert J.: Polimery 2008, 53, 591.

21. Schlemmer D., Anielica R. S., Sales M. J. A.: Compos. Struct. 2010, 92, 2066.

22. Tang X., Alavi S. i in.: Carbohydr. Polym. 2008, 74, 552.

23. Bagdi K., Mulle P.: Compos. Interfaces 2006, 13, 1.

24. Zhong J., Lin G. i in.: Macromolecules 2002, 35, 4481.

25. Zhang J., Lou J. i in.: Polymer 2008, 49, 2381.

26. Kozakiewicz J., Kuczyñska H., Jesionowski T., Nowakowski R. i in.: Inż. Mater. 2007, 5, 863.

27. Zgłosz. pat. P-392 109 (2010).

28. Jeziórska R.: Int. Polym. Proc. 2007, 22, 122.

29. Pat. USA 3 898 300 (1987).

30. Pat. USA 5 223 586 (1993).

31. Zgłosz. pat. P- 386 832 (2008).

32. Zgłosz. pat. P- 392 423 (2010).

33. Świerz-Motysia B., Jeziórska R., Szadkowska A.: Czasopismo Techn. 2009, 106 (3), 337.

34. Wunderlich B.: „Macromolecular Physics”, Tom I, Academic Press INC, Nowy Jork–Londyn 1973, str. 401—404.

35. Riga A., Hang J.: J. Therm. Anal. Calorim. 2004, 75, 257.

36. Poutanten K., Forssell P.: Trends Polym. Sci. 1996, 4, 128.

37. Wilpiszewska K., Spychaj T.: Polimery 2006, 51, 327.

Google Scholar

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0

R. Jeziórska polimery@ichp.pl

A. Szadkowska

B. Świerz-Motysia

J. Kozakiewicz