The influence of temperature of poly(vinyl chloride) melt on the equilibrium state of gelation process

K. Piszczek; J. Tomaszewska; T. Sterzyński

Published : 2020-02-28

Vol. 55 No. 2 (2010)

The influence of temperature of poly(vinyl chloride) melt on the equilibrium state of gelation process

K. Piszczek J. Tomaszewska T. Sterzyński

Abstract

The final stage of PVC gelation during kneading until the moment of equilibrium state of the torque has been discussed. The processing of unplastified PVC compounds was carried out in the Brabender mixing chamber at chamber temperature (Tch) 150, 160, 170, 175, 180, 185 or 200° and at rotational speed of the blades: 5, 10, 20, 30 or 40min-1 (for the temperature 150° also rotational speed 50 or 60min-1 was used). The shear rate values from 2.18 to 26.04s-1 corresponded with the range of rotational speed mentioned above. The change of the real temperature of the compound during kneading (TE) and its effect on PVC gelation degree (G) were analyzed. A progress of gelation was studied using MFR measurements and SEM observations. It was found that TE value affects the degree of gelation at the last stage of kneading while the effect of residence time of the compound in the chamber (tE) appeared to be insignificant. Apart from the high gelation level, revealed by DSC and MFR results, the processing at high shear rate leads to significant inhomogenenity confirmed by SEM method.

Keywords

poli(chlorek winylu) ; żelowanie ; mieszanie ; moment obrotowy ; struktura ; wskaźnik szybkości płynięcia poly(vinyl chloride) ; gelation ; mixing ; torque ; structure ; melt flow rate

Details

References

Statistics

Authors

Download files

PDF

Zasady cytowania

Piszczek, K., Tomaszewska, J., & Sterzyński, T. (2020). The influence of temperature of poly(vinyl chloride) melt on the equilibrium state of gelation process. Polimery, 55(2), 106-110. Retrieved from https://ichp.vot.pl/index.php/p/article/view/992

References

Gilbert M: . M. S. - Rev. Macromol. Chem. Phys. 1994, C34,Nol, 77.

2. Fillot L. A., Hajji P., Gauthier C, Masenelli-Varlot K.: J. Vinyl Add. Technol. 2006,12, 98.

3. Chen C. H., Wesson R. D., Collier J. R., Lo Y.-W.: J. Appl. Polym. Sci 1995, 58,1093.

4. Piszczek K.: Zeszyty Naukowe IPTS, Numer Specjalny 06.2007, ISNN 1429-0472, ISBN 978-83-917--693-6-2,167.

5. Bortel K., Szewczyk P.: Polimery 1993, 38,578.

6. Zajchowski S., Piszczek K., Tomaszewska J.: Polimery 2001,46,232.

7. Summers J. W., Rabinovitch E. B.: J. Macromol Sci. Phys. 1981, B20, No 2,219.

8. Faulkner P. G.: J. Macromol. Sci. Phys. 1975, Bll, No 2, 251.

9. Yu A., Boulier P., Sandhu A.: J. Vinyl Technol 1984,6, 110.

10. Krzewki R. J., Collins E. A.: J. Macromol Sci. Phys. 1981, B20, No 4,443.

11. Piszczek K., Tomaszewska J., Sterzynski T: Polimery 2004,49,646.

12. Tomaszewska J., Sterzynski T, Piszczek K.: Polimery 2008,53,678.

13. Tomaszewska J., Sterzynski T, Piszczek K.: J. Appl Polym. Sci. 2004, 93, 966.

14. Tomaszewska J., Sterzynski T, Piszczek K.: J. Appl Polym. Sci. 2007,103,3688.

15. Tomaszewska J., Sterzynski T, Piszczek K.: J. Appl Polym. Sci. 2007,106,3158.

16. Potente H., Schultheis S. M.: Kunststoffe 1987,77,401.

17. Piszczek K., Skorczewska K., Sterzynski T: Polimery 2009,54,296.

18. Parey J., Kruger E.: Kunststoffe 1984,74, 39.

19. Zajchowski S., Piszczek K., Skraga J.: Przem. Chem, 1987, 66, 338.

20. Terselius B., Jansson J. F: Plast. Rubb. Proc. Appl. 1985, 5,193.

Google Scholar

Citing articles via

Statistics

Total abstract views : 72

PDF Downloads : 37