Epoxy resin compositions containing liquid phosphorus flame retardants used in infusion technology

Rafał Oliwa

doi:10.14314/polimery.2020.7.12

Published : 2020-12-16

Vol. 65 No. 7-8 (2020)

Epoxy resin compositions containing liquid phosphorus flame retardants used in infusion technology

Rafał Oliwa

DOI: https://doi.org/10.14314/polimery.2020.7.12

Abstract

This study investigates the impact of the type and amount of liquid phosphorus flame retardant additive on the flammability and mechanical properties of epoxy compositions dedicated to the infusion process. To this purpose, epoxy resin (EP) compositions containing 10 and 20 wt % of liquid ammonium polyphosphate (APPL) and dimethyl methylphosphonate (DMMP) were obtained. Mechanical properties and flame resistance of obtained epoxy compositions were determined in terms of their use as a matrix in laminate infusion technology. Based on the results obtained, it was found, that the flame resistance increases, while the mechanical properties decreases with flame retardant loading. The best flame resistance results were obtained for a composite containing 20 wt % APPL: limiting oxygen index LOI = 23.9% instead of 19.8% – EP, peak of heat release rate pHRR = 427.3 kW/m2 instead of 1046.3 kW/m2 – EP.

Keywords

composites ; epoxy resin ; infusion ; liquid flame retardants kompozyty ; żywica epoksydowa ; infuzja ; ciekłe uniepalniacze

Details

References

Statistics

Authors

Download files

PDF

Zasady cytowania

Oliwa, R. (2020). Epoxy resin compositions containing liquid phosphorus flame retardants used in infusion technology. Polimery, 65(7-8), 578-581. https://doi.org/10.14314/polimery.2020.7.12

References

Chi Z., Guo Z., Xu Z. et al.: Polymer Degradation and Stability 2020, 176, 109151. h t t p://d x . d o i . o r g / 10 .1016/ j .p o l y md e g r a d -stab.2020.109151

[2] Back J-H., Baek D., Kim T. et al.: International Journal of Adhesion and Adhesives 2020, 100, 102601.
Crossref

[3] Jeng R.-J., Shau S.-M., Lin J.-J. et al.: European Polymer Journal 2002, 38, 683.
Crossref

[4] Oliwa R., Oleksy M., Oliwa J. et al.: Polimery 2019, 64, 290.
Crossref

[5] Oliwa R., Oleksy M., Czech-Polak J. et al.: Journal of Fire Sciences 2019, 37, 155.
Crossref

[6] Chen Z., Jiang M., Zhang Q. et al.: International Journal of Polymer Analysis and Characterization 2017, 22, 509.
Crossref

[7] Zheng T., Ni X.: RSC Advances 2016, 6, 57122.
Crossref

[8] Xu Z., Duan L., Hou Y. et al.: Composites Part A: Applied Science and Manufacturing 2020, 131, 105815.
Crossref

[9] Oliwa R., Bulanda K., Oleksy M. et al.: Polimery 2020, 65, 387.
Crossref

[10] Rajaei M., Wang D.-Y., Bhattacharyya D.: Composites Part B: Engineering 2017, 113, 381.
Crossref

[11] Szolnoki B., Toldy A., Konrád P. et al.: Periodica Polytechnica Chemical Engineering 2013, 57, 85.
Crossref

[12] Lim Patrick W.K., Mariatti M., Chow W.S., Mar K.T.: Composites Part B: Engineering 2012, 43, 124.
Crossref

[13] Wu K., Zhang Y.-K., Zhang K. et al.:. Journal of Analytical and Applied Pyrolysis 2012, 94, 196.
Crossref

[14] Schartel B., Hull T.R.: Fire and Materials 2007, 31, 327.
Crossref

[15] Zhao C., Li Y., Xing Y. et al.: Journal of Applied Polymer Science 2014, 131, 40218.
Crossref

[16] Oliwa R., Heneczkowski M. Oleksy M., Galina H.: Composites Part B: Engineering 2016, 95, 1.
Crossref

[17] Liu L., Zhang Y., Li L., Wang Z.: Polymers for Advanced Technologies 2011, 22, 2403.
Crossref

Google Scholar

Altmetric indicators

Citing articles via

CITEDBY SCOPUS

Statistics

Total abstract views : 189

PDF Downloads : 228