Aging behavior of three-proof polyurethane coatings under UV radiation

Jianfa Wang; Zheng Gu; Jie  Zhao; Susu Zhang; Peiyao Li; Chao  Meng; Jinyong  Sui; Xiaoyi Zhang; Shaokai Hu; Jiaying Pan; Junyi Li

doi:10.14314/polimery.2022.9.4

Data publikacji : 2022-09-29

Tom 67 Nr 9 (2022)

Wpływ promieniowania UV na starzenie potrójnych powłok poliuretanowych

Jianfa Wang https://orcid.org/0000-0002-1242-3794 Zheng Gu https://orcid.org/0000-0001-9521-2863 Jie Zhao Susu Zhang https://orcid.org/0000-0003-3620-0816 Peiyao Li https://orcid.org/0000-0002-4713-1599 Chao Meng https://orcid.org/0000-0001-6603-2273 Jinyong Sui https://orcid.org/0000-0002-4232-3540 Xiaoyi Zhang https://orcid.org/0000-0003-4047-5046 Shaokai Hu https://orcid.org/0000-0001-6603-2273 Jiaying Pan https://orcid.org/0000-0002-1609-7869 Junyi Li https://orcid.org/0000-0001-8110-6496

DOI: https://doi.org/10.14314/polimery.2022.9.4

Abstrakt

Przeprowadzono badania wpływu promieniowania UV na właściwości fizyczne i mechaniczne żywic poliuretanowych oraz potrójnych poliuretanowych powłok ochronnych. Określono zmiany połysku żywic i powłok podczas starzenia pod podczas naświetlania promieniowaniem UV oraz wpływ tego procesu na właściwości mechaniczne badanych materiałów. Zbadano strukturę materiałów za pomocą mikroskopii skaningowej SEM oraz spektroskopii w podczerwieni z transformacją Fouriera FTIR, wykonano również badania termograwimetryczne TGA i DTG. Okazało się, że połysk gotowych powłok ochronnych jest gorszy aniżeli połysk pojedynczych żywic, natomiast starzenie znacznie go pogarsza (przy naświetlaniu przez 1200 godzin, w przypadku żywic z 81,3° do 8,9°, zaś w przypadku powłok z 61,1° do 2,8°). Wytrzymałość na rozciąganie żywic pogarsza się w trakcie starzenia, zaś wartość wydłużenia przy zerwaniu osiąga minimum przy czasie naświetlania 100 godzin. W przypadku powłok zarówno wartości wytrzymałości na rozciąganie, jak i wydłużenia przy zerwaniu w trakcie starzenia najpierw maleją, a potem rosną, osiągając minimum przy czasie naświetlania 800 godzin; przy długim czasie naświetlania powyżej 1200 godzin właściwości te ponownie ulegają pogorszeniu.

Słowa kluczowe

polyurethane ; ultraviolet ; coating ; resin poliuretan ; ultrafiolet ; powłoka ; żywica

Szczegóły

Bibliografia

Wskaźniki

Autorzy

Pobierz pliki

PDF (English)

Zasady cytowania

Wang, J., Gu, Z., Zhao, J. ., Zhang, S., Li, P., Meng, C. ., Sui, J. ., Zhang, X., Hu, S., Pan, J., & Li, J. (2022). Wpływ promieniowania UV na starzenie potrójnych powłok poliuretanowych. Polimery, 67(9), 433-442. https://doi.org/10.14314/polimery.2022.9.4

Bibliografia

Yang F., Lv Y.B., Yang X. et al.: Comprehensive Corrosion Control 2016, 5, 78.
Crossref Google Scholar

Li Q., Li H., Li C. et al.: Coating Industry 2018, 48(09), 46. Google Scholar

Zhang Y., Cheng Z., Liu H.: Equipment Environmental Engineering 2018, 15(2), 97. Google Scholar

Luo L., Xiao Y., Su Y. et al.: Equipment Environmental Engineering 2015, 12(6), 42. Google Scholar

Yang X.F., Tallman D.E., Bierwagen G.P. et al.: Polymer Degradation and Stability 2002, 77, 103.
Crossref Google Scholar

Yang X.F., Li J., Croll S.G. et al.: Polymer Degradation and Stability 2003, 80, 51.
Crossref Google Scholar

Xu Y., Yan C., Ding J. et al.: Chinese Journal of Corrosion and Protection 2004, 24(3), 168. Google Scholar

Yang H., Wang X., Zheng J. et al.: Journal of Xiamen University (Natural Science Edition) 2017, 56(03), 370. Google Scholar

Zhang H., Xin L., Hong L.: China Adhesive 2018, 27(03), 51.
Crossref 10.13416/j.ca.2018.03.013 Google Scholar

Xu X., Zou B., Lin Z.: China Adhesives 2016, 25(11), 37 + 59.
Crossref Google Scholar

Zhang H., Xin C., Li S. et al.: Polyurethane Industry 2016, 31(05), 14. Google Scholar

Pan Y., Wen Q., Zhu J.: Surface Technology 2020, 49(06), 305-313 + 344.
Crossref Google Scholar

Pat. GB / T 23987-2009. Google Scholar

Pat. GB / T 1766-1995. Google Scholar

Civancik-Uslu D., Ferrer L., Puig R. et al.: Science of the Total Environment 2018, 626, 927.
Crossref Google Scholar

Wskaźniki altmetryczne

Cytowania w Google Scholar

CITEDBY SCOPUS

Statystyki

Total abstract views : 176

PDF Downloads : 97

Jianfa Wang wjf19511638332@163.com
https://orcid.org/0000-0002-1242-3794

Afiliacja
College of Chemistry and Chemical Engineering, Qingdao University, China 266071

Zheng Gu
https://orcid.org/0000-0001-9521-2863

Afiliacja
College of Chemistry and Chemical Engineering, Qingdao University, China 266071

Jie Zhao

Afiliacja
College of Chemistry and Chemical Engineering, Qingdao University, China 266071

Susu Zhang
https://orcid.org/0000-0003-3620-0816

Afiliacja
College of Chemistry and Chemical Engineering, Qingdao University, China 266071

Peiyao Li
https://orcid.org/0000-0002-4713-1599

Afiliacja
College of Materials Science and Engineering, Qingdao University, China 266071

Chao Meng
https://orcid.org/0000-0001-6603-2273

Afiliacja
College of Chemistry and Chemical Engineering, Qingdao University, China 266071

Jinyong Sui
https://orcid.org/0000-0002-4232-3540

Afiliacja
College of Chemistry and Chemical Engineering, Qingdao University, China 266071

Xiaoyi Zhang
https://orcid.org/0000-0003-4047-5046

Afiliacja
College of Chemistry and Chemical Engineering, Qingdao University, China 266071

Shaokai Hu
https://orcid.org/0000-0001-6603-2273

Afiliacja
College of Chemistry and Chemical Engineering, Qingdao University, China 266071

Jiaying Pan
https://orcid.org/0000-0002-1609-7869

Afiliacja
College of Materials Science and Engineering, Qingdao University, China 266071

Junyi Li
https://orcid.org/0000-0001-8110-6496

Afiliacja
College of Materials Science and Engineering, Qingdao University, China 266071