Uretanowe elastomery magnetoreologiczne aktywowane polem magnetycznym

A. Boczkowska; S. Awietjan

Published : 2009-01-10

Vol. 54 No. 1 (2009)

Magnetorheological urethane elastomers activated by magnetic field

A. Boczkowska S. Awietjan

Abstract

Urethane and urea-urethane segmental elastomers (EPU 1,1 and EPU 1,25) were synthesized and selected properties of them were compared with those of polyurethane gels (PU 80/20 and PU 70/30) prepared by mixing of commercial products (Table 1). Various amounts of ferromagnetic particles (carbonyl iron) were added to elastomers preparing in this way magnetorheological urethane elastomers (MRE). They were cured in magnetic field and column arrangement of Fe particles has been obtained. The effects of conditions of MRE preparation on their structures were evaluated using transmission microscopy and SEM and significant dependence on the amount of Fe particles in a composite was found (Fig. 1, 2). For Fe amount higher than 11.5 vol. % the structure looks like a net. Magnetic properties of MRE obtained were investigated by VSM method in directions parallel and perpendicular to magnetic particles arrangement (Fig. 5). The changes of properties depend on the composite structure and the power of external magnetic field applied, causing an increase in shear modulus (Fig. 3, 4, 6).

Keywords

poliuretany ; elastomery magnetoreologiczne ; żelazo karbonylkowe ; właściwości reologiczne ; właściwości mechaniczne polyurethanes ; magnetorheological elastomers ; carbonyl iron ; rheological properties ; mechanical properties

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Boczkowska, A., & Awietjan, S. (2009). Magnetorheological urethane elastomers activated by magnetic field. Polimery, 54(1), 26-30. Retrieved from https://ichp.vot.pl/index.php/p/article/view/1173

References

Zhou G. Y.: Smart. Mater. Struci. 2003,12,139. Google Scholar

Farshad M., Benine A.: Polym. Test. 2004, 23, 347. Google Scholar

Jolly M. R., Carlson J. D., Munoz B. C., Bullions T. A.: J. Intell. Mater. Syst. Struci. 1996,7, 613. Google Scholar

Kankanala S. V., Triantafyllidis N.: J. Mech. Phys. So-lids 2004,52, 2869. Google Scholar

Khoo M., Liu C.: Sens. Actuators, A 2001, 89, 259. Google Scholar

Yicente J., Bossis G., Lacis S., Guyot M.: J. Magn. Magn. Mater. 2002, 251,100. Google Scholar

An Y, Shaw M. T.: Smart. Mater. Struci. 2002,12,157. Google Scholar

Kallio M., Aalto S., Lindroos T.: „Preliminary test on a MRĘ device", „AMAS Workshop on Smart Materials and Structures SMART '03", Jadwisin 2—5 września 2003, mat. konf. str. 353—360. Google Scholar

Boczkowska A., Awietjan S. R, Babski K., Wróblewski R., Leonowicz M.: „Effect of the processing condi-tions on the microstructure of urethane magneto-rheological elastomers", mat. konf. „Smart Structures and Materials 2006: Active Materials: Behavior and Mechanics", Proceedings of SP1E CD, t. 6170, nr 28. Google Scholar

Altmetric indicators

Citing articles via

Statistics

Total abstract views : 20

PDF Downloads : 8