Synteza i właściwości poliuretanów otrzymanych z glikolizatów uzyskiwanych z odpadowej pianki polieterouretanowej

J. Datta; K. Pniewska

Published : 2022-08-23

Vol. 53 No. 1 (2008)

Syntheses and properties of polyurethanes got from glycolysis products obtained from waste polyurethane foams

J. Datta K. Pniewska

Abstract

The course of waste polyurethane foam glycolysis with 1,4-butylene glycol (BDO) or polyoxyethylene glycol (PEG 300), dependently on PUR foam:glycol weight ratio and the kind of glycolysis agent, was investigated (Table 1, Fig. 1 and 2). Urethane prepolymer obtained from 4,4'-methylene-diphenyldiizocyanate (MDI) and oligo(ethylene-butylene adipate) ("Poles 55/20") was then extended either with the mixture of glycolysis product with BDO or PEG 300 or with the glycolysis product itself (Table 2). The following properties of PUR obtained were measured: storage modulus (E'), tensile properties and hardness, dependently on the type of glycolysis product used (Fig. 3-6). It was found that use of glycolysis products in PUR syntheses improved their thermo-mechanical strength (expressed with E' value) at temperature below zero as well as tension set at break and hardness.

Keywords

poliuretany ; odpadowa pianka ; glikoliza ; synteza ; właściwości wytrzymałościowe polyurethanes ; waste foam ; glycolysis ; synthesis ; tensile properties

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Datta, J., & Pniewska, K. (2022). Syntheses and properties of polyurethanes got from glycolysis products obtained from waste polyurethane foams. Polimery, 53(1), 27–32. Retrieved from https://ichp.vot.pl/index.php/p/article/view/1282

References

Błędzki A. K., Pawluczuk K.: Polimery 1994, 39, 345.

2. Prociak A., Pielichowski J.: "Modyfikacja piankowych systemów poliuretanowych produktami glikolizy", Konferencja naukowa "Recykling tworzyw sztucznych R'02", 16--20.09.2002 r. Jasenik, Czechy.

3. Kowalska E., Choroś M., Kuczyńska L., Wielgosz Z.: Polimery 2006, 51, 671.

4. Jeziórska R.: Polimery 2005, 50, 468.

5. Borda J., Pasztor G., Zsuga M.: Polym. Degrad. Stabil. 2000, 68, 419.

6. Pat. USA 5 357 006 (1994).

7. Modesti M., Simioni F.: Polym. Eng. Sci. 1996, 36, 17.

8. Prociak A., Pielichowski J.: Polimery 2005, 50, 682.

9. Datta J., Rohn M.: Polimery 2007, 52, 579.

10. Datta J., Rohn M.: Polimery 2007, 52, nr 9.

11. Datta J., Pasternak S.: "Synteza oraz właściwości oligouretanodioli i uzyskanych z nich poliuretanów", XVI Konferencja Naukowa "Modyfikacja polimerów", Polanica Zdrój 23--26 września 2003 r.

12. Datta J., Pasternak S.: Polimery 2005, 50, 682.

Google Scholar

Altmetric indicators

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0