Ocena poprawek w pomiarach reometrycznych polietylenu. Cz.II. Wykładnik płynięcia, poprawka Rabinowitscha

A. Kloziński; T. Sterzyński

Published : 2022-08-26

Vol. 52 No. 11-12 (2007)

Evaluation of correction factors in rheological investigations of polyethylene. Part II. Power low index, Rabinowitsch correction

A. Kloziński T. Sterzyński

Abstract

The results of investigation of the effect of Rabinowitsch correction on the courses of flow curves and viscosity curves for two polyethylene grades (PE-LD and PE-MD) as well as their blend in the ratio 1:1 were presented (Table 1, Fig. 1-6). Rheological investigations were performed in the real conditions of extrusion process, using extrusion rheometer and cylindrical dies of circular cross-sections and various L/D ratios (Table 2 and 3). Power low index n was found to vary from 0.28 to 0.86 (Table 5), dependently on the system investigated. The differentiation in power low index values is due to different values of shear stress ... and various ranges of uncorrected shear rate during the polymer flow through the die of defined length and diameter. The application of real n-values in evaluation of the Rabinowitsch correction factor, related to changes of viscosity in the range of 75% relative to non corrected values, reveals in a significant viscosity curves shift. Experimentally determined rheological values (power low index, Rabinowitsch correction, shear stress, corrected shear rate, apparent viscosity and corrected viscosity) are given in Tables 5-7.

Keywords

pomiary reologiczne ; polietylen ; poprawka Rabinowitscha ; wykładnik płynięcia n ; krzywa płynięcia ; krzywa lepkości rheological measurements ; polyethylene ; Rabinowitsch correction ; power low index n ; flow curve ; viscosity curve

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Kloziński, A., & Sterzyński, T. (2022). Evaluation of correction factors in rheological investigations of polyethylene. Part II. Power low index, Rabinowitsch correction. Polimery, 52(11-12), 855–862. Retrieved from https://ichp.vot.pl/index.php/p/article/view/1481

References

Kembłowski Z.: "Reometria płynów nienewtonowskich", WNT, Warszawa 1973, str. 27--100.

2. Sikora R.: "Podstawy przetwórstwa tworzyw polimerowych", Wydawnictwo Uczelniane Politechniki Lubelskiej, Lublin 1992, str. 145--244.

3. Sikora R.: "Leksykon naukowo-techniczny. Wprowadzenie do przetwórstwa tworzyw polimerowych", Wadim Plast Sp. J., Lublin 2002.

4. Praca zbiorowa: "Przetwórstwo tworzyw polimerowych. Podstawy logiczne, formalne i terminologiczne" (red. Sikora R.), Wydawnictwo Politechniki Lubelskiej, Lublin 2006, str. 99--127, 467--514.

5. Kloziński A., Sterzyński T.: IX Profesorskie Warsztaty Naukowe "Przetwórstwo tworzyw Polimerowych", Szczecin--Dziwnówek 2004, Wydawnictwo Politechniki Szczecińskiej, Szczecin 2004, str. 53--54.

6. Kloziński A., Sterzyński T.: Polimery 2005, 50, 455.

7. Kloziński A., Sterzyński T.: Polimery 2007, 52, 583.

8. Szlezyngier W.: "Podstawy reologii polimerów", Politechnika Rzeszowska 1994, str. 48--69.

9. Rabinowitsch B.: Z. Physik. Chem. 1929, 145A, 1.

10. Mooney M.: J. Rheology 1931, 2, 210.

11. Wilczyński K.: "Reologia w przetwórstwie tworzyw sztucznych", WNT, Warszawa 2001, str. 99--125.

12. Laun H. M.: Rheol. Acta. 2004, 43, 509.

13. Robert L., Demay Y., Vergnes B.: Rheol. Acta 2004, 43, 89.

14. Schramm G.: "A Practical Approach to Rheology and Rheometry", Gebrueder HAAKE GmbH, Karlsruhe 1994, str. 3--27, 207--214 (tłum. polskie "Reologia. Podstawy i zastosowania", Ośrodek Wydawnictw Naukowych PAN, Poznań 1998, str. 13--34, 191--197).

15. Birley A. W., Haworth B., Batchelor J.: "Physics of Plastics -- Processing, Properties and Materials Engineering", Hanser Publishers Münnich, Vienna, New York, Barcelona 1992, str. 59--91.

16. Liang Ji.-Z.: Polym. Test. 2002, 21, 307.

17. Nakason C. i in.: Polym. Test. 2002, 21, 449.

18. Abraham D.: Polymer 1998, 39, nr 1, 117.

19. Chhabra R. P., Richardson J. F.: "Non-Newtonian Flow in the Process Industries -- Fundamentals and Engineering Applications", Butterworth -- Heinemann 1999, str. 37--41.

20. Kloziński A., Kruszelnicka I., Sterzyński T.: w pracy zbiorowej "Postęp w przetwórstwie materiałów polimerowych" (red. Koszkul J.), Wydawnictwo Politechniki Częstochowskiej, Częstochowa 2002, str. 264--272.

21. Kloziński A., Sterzyński T.: "The Rheological Properties Measurements in a Real Extrusion Line", 21st Annual Meeting of the Polymer Processing Society, Leipzig 2005.

22. Kloziński A.: Zeszyty Naukowe nr 246 -- Chemia i Technologia Chemiczna 11, Wydawnictwo Uczelniane Akademii Techniczno-Rolniczej, Bydgoszcz 2006, str. 69--72.

23. Kloziński A., Sterzyński T.: w [22], str. 73--77.

24. Wagner N. J., Prud'homme R. K.: Current Opinion & Interface Sci. 2001, 6, 421.

25. Agassant J.-F. i in.: "Polymer Processing -- Principles and Modeling", Hanser Publishers 1991, str. 41--89.

Google Scholar

Altmetric indicators

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0

A. Kloziński Arkadiusz.Klozinski@put.poznan.pl

Affiliation
Politechnika Poznańska, Instytut Technologii i Inżynierii Chemicznej, Zakład Polimerów, Pl. M. Skłodowskiej-Curie 2, 60-965, Poznań,

T. Sterzyński