Mechanical properties of poly(vinyl chloride) of defined gelation degree

S. Zajchowski

Published : 2022-09-01

Vol. 50 No. 11-12 (2005)

Mechanical properties of poly(vinyl chloride) of defined gelation degree

S. Zajchowski

Abstract

The effect of processing temperature (140-205 °C) on gelation degree (G) of unplasticized PVC of K value = 61, containing 8 wt. % of ethylene/vinyl acetate copolymer, has been studied using three various measuring tools: weight plastometer, capillary rheometer and screw capillary rheometer. It was found that independently on the method used all of measuring points lay on the one curve. The dependence of G value on the composition of the mixture of non-gelated (A) and fully gelated (B) PVC granulated products in the whole range of their compositions has been determined using the methods mentioned above. The following properties of the extrudates were tested: impact strength, tensile strength and relative elongation at break. There was found the possibility of determination of mechanical properties of an extrudate via proper selection of processing temperature and the composition of PVC granulated products, showing various gelation degrees.

Keywords

poli(chlorek winylu) ; stopień zżelowania ; temperatura wytłaczania ; właściwości mechaniczne poly(vinyl chloride) ; gelation degree ; processing temperature ; mechanical properties

Details

References

Statistics

Authors

Download files

PDF

Zasady cytowania

Zajchowski, S. (2022). Mechanical properties of poly(vinyl chloride) of defined gelation degree. Polimery, 50(11-12), 890-893. Retrieved from https://ichp.vot.pl/index.php/p/article/view/1702

References

Materiały konferencyjne, “Wood-Plastic Composites”, Wien 2003.

2. Materiały konferencyjne, “5th Global Wood and Natural Fibre Composites Symposium”, Kassel 2004.

3. Patuszyńska I., Zajchowski S., Patuszyński K.: Inż. i Ap. Chem. 2005, 44, 3, 57.

4. Kuciel S., Liber A.: Polimery 2005, 6, 436.

5. Zajchowski S., Patuszyński K.: Kompozyty (Composites) 2005, 5, 3, 35.

6. Zajchowski S.: Chemik 2004, 57, 1, 15.

7. Zajchowski S, Głowacka L.: “Nowe kierunki modyfikacji i zastosowań tworzyw sztucznych”, red. J. Jurga, B. Jurkowski, T. Sterzyński, Wyd. Politechniki Poznańskiej, Poznań 2004, 71.

8. Zajchowski S.: “Wpływ charakteru ziaren poli(chlorku winylu) na właściwości reologiczne i strukturę morfologiczną plastyfikatów”, praca doktorska, UMK Toruń 1977.

9. Świerz-Motysia B., Pielichowski K.: Polimery 2005, 50, 601.

10. Piszczek K., Tomaszewska J., Sterzyński T.: Polimery 2004, 49, 646.

11. Obłój-Muzaj M., Świerz-Motysia B., Szabłowska B.: “Polichlorek winylu”, WNT Warszawa 1997.

12. Abramowicz A.: Polimery 2005, 50, 593.

13. Benjamin P.: Conference “PVC Processing”, Egham 1978, B5.1.

14. Piszczek K.: Polimery 2005, 56, 441.

15. Zajchowski S., Tomaszewska J., Piszczek K.: IX Seminarium “Tworzywa sztuczne w budowie maszyn”, Kraków 2000, 377.

16. Tomaszewska J., Piszczek K., Zajchowski S.: IX Seminarium “Tworzywa sztuczne w budowie maszyn”, Kraków 2000, 341.

17. Zajchowski S., Piszczek K., Tomaszewska J.: Polimery 2001, 46, 232.

18. Menges G., Parey J., Zajchowski S.: Raport z prac, Institut für Kunststoffverarbeitung RWTH, Aachen 1980.

19. Tomaszewska J.: “Reometryczna i strukturalna analiza procesu żelowania nieplastyfikowanego polichlorku winylu”, praca doktorska, Politechnika Poznańska, 2005.

20. Parey J., Zajchowski S.: Plastverarbeiter 1981, 32, 724.

21. Zajchowski S., Parey J.: Raport z prac, Institut für Kunststoffverarbeitung RWTH, Aachen 1981.

22. Lamberty M.; Plast. Modern. Elast. 1974, 26, 82.

23. Sikora R.: Podstawy przetwórstwa tworzyw wielkocząsteczkowych, Wydawnictwa Uczelniane, Politechnika Lubelska, Lublin 1992.

24. Kloziński A., Sterzyński T.: Polimery 2005, 50, 455.

25. Stabik J.: Polimery 2004, 49, 712.

26. Stabik J.: Polimery 2004, 49, 634.

27. Jeziórska R.: Polimery 2004, 49, 623.

28. Stasiek J.: Polimery 2003, 48, 443.

Google Scholar

Citing articles via

Statistics

Total abstract views : 49

PDF Downloads : 39