Thermal stability of poly(L-lactide) prepared by polymerization of L,L-dilactide with Sn(ll)-based initiators

J. Libiszowski; A. Kowalski; T. Biela; A. Duda

Published : 2022-09-01

Vol. 49 No. 10 (2004)

Thermal stability of poly(L-lactide) prepared by polymerization of L,L-dilactide with Sn(ll)-based initiators

J. Libiszowski A. Kowalski T. Biela A. Duda

Abstract

alpha-Ester-omega-hydroxy terminated poly(L-lactide) [C4H9OC(O)-PLA-OH] was prepared by the ring-opening polymerization of L,L-dilactide using tin(II) 2-ethylhexanoate (tin octoate, Sn(Oct)2]/BuOH system or tin(ll) butoxide as initiators in a wide range of molecular weights (M,(n)): from 10(3) up to 7 ź 10(5). Thermal degradation behavior of C4H9OC(O)-PLA-OH was then compared with that of its esterified counterpart [C4H9OC(O)-PLA--OC(O)CH(C2H5)C4H9). Thermogravimetric measurements versus M(n) revealed, as a result of Mn -> infinity extrapolation, the upper limit of thermal resistance of poly(L-lactide) (PLA). The onset temperature of the thermal degradation (OT) and the temperature of maximum degradation rate (MDT) of PLA are equal to 337 and 376 °C, respectively. Despite the deteriorating effect on the PLA molecular weight caused by in situ esterification of the hydroxyl chain ends with Sn(Oct)2, largely unreacted in polymerization, certain improvement of PLA thermal stability due to this side reaction was also observed.

Keywords

L,L-dilaktyd ; poli(L-laktyd) ; butanolan cyny(II) ; oktanian cyny(II) ; mechanizm polimeryzacji ; estryfikacja poli(L-laktydu) L,L-dilactide ; poly(L-lactide) ; tin(II) butoxide ; tin(ll) octoate ; polymerization mechanism ; poly(L-lactide) esterification ; thermal degradation

Details

References

Statistics

Authors

Download files

PDF

Zasady cytowania

Libiszowski, J., Kowalski, A., Biela, T., & Duda, A. (2022). Thermal stability of poly(L-lactide) prepared by polymerization of L,L-dilactide with Sn(ll)-based initiators. Polimery, 49(10), 690–697. Retrieved from https://ichp.vot.pl/index.php/p/article/view/1801

References

l. Zhang X., Wyss U. P., Pichora D., Goosen M. F. A.: J. Macromol. Sci. - Pure Appl. Chem. 1993, A30, 933.

2. Kharas G. B., Sanchez-Riera F., Severson D. K.: "Polymers of Lactic Acid" in: "Plastics frorn Microbes" (Ed. Mobley D. P.), Hauser Publishers, Munich, Vienna, rew York] 994, p. 93.

3. Hartmann M. H.: "High Molecular Weight Polylactic Acid Polymers" in: "Biopolymers frorn Renewable Resollrces" (Ed. Kapłan D. L.), Springer, Berlin 1998, p.367.

4. Gruber P., O'Brien M.: "Polylactides NatureWorks PLA" in: "Biopolymers", Vol. 4: "Polyesters III -Applications and Commercial Products" (Ed, Steinbiichel A., Doi Y), Wiley- VCH, Weinheim 2002, p.235.

5. Kawashima N., Ogawa Sh., Obuchi Sh., Matsuo M., Yagi T.: "Polylactic Acid LACEA" in: 141, p. 251.

6. Duda A., Penczek S.: Polimery 2003, 48, 16.

7. Jamshidi K., Hyon S.-H., lkada Y.: Polymer 1988, 29, 2229.

8. Zhang X, Wyss U. P., Pichora D., Goosen M. F. A.: Polym. Bull. 1992,27,623.

9. Kopinke F-D., Remmler M., Mackenzie K., Moder M., Wachsen O.: Potym. Degrad. Stab. 1996,53,329.

10. Wachsen O., Reichert K. H., Kriiger R. P., Much H., Schulz G.: Polym. Degrad. Slab. 1997,55,225.

11. Degee P., Dubois P., Jerome R.: Macromol. Chem. Phys. 1997, 198, 1985.

12. Carn D., Marucci M.: Polymer 1997, 38,1879.

13. Lee S.-H., Kim S. H., Han Y.-K., Kim Y. H.: J. Polym. Sci.-: Part A: Polym. Chem. 2001, 39, 973.

14. Aoyagi Y., Yamashita K., Doi Y.: Polym. Degrad. Slab. 2002, 76,53.

15. Zhao J.-L., Cai Q., Jiang L Shuai X.-T., Bei J.-Z., Chen Ch.-W., Xi F: Poluiner 2002, 43, 5819.

16. Sodergard A., Stolt M.: Progr. Polym. Sci. 2002, 27, 1144.

17. Nishida H., Mori T., Hoshihara S., Fan Y. L Shirai Y., Endo T.: Polym. Oegrad. Slab. 2003,81,515.

18. Mecerteyes D., Jerorne R., Dubois P.: Adv. Polym. Sci. 1998,147,1.

19. Duda A., Penczek S.: "Mechanisms of Aliphatic Polyester Forrnation" in: "Biopolymers", Vol. 3b. "Polyesters II - Properties and Cheruical Synthesis" (Ed. Steinbuchcl A., Doi Y), Wiley-VCH, Weinheim 2002, p. 371.

20. Kowalski A., Duda A., Fenczek S.: Macramol. Rapid Commun. 1998,19,567.

21. Kowalski A, Duda A, Penczek 5.:Macromolecules 2000,33,689.

22. Kowalski A., Duda A., Penczek S.: Macromolecules 2000,33,7359.

23. Libiszowski J., Kowalski A, Duda A., Penczek S.: Macromol. Chem. Phys. 2002, 203, 1694.

24. Duda A, Kowalski A, Libiszowski J.: Polimery 2000, 45,465 .

25. Gsell R., Zeldin M.: J. Inorg. Nucl. Chem. 1975, 37, 1133.

26. Kowalski A, Libiszowski J., Duda A., Penczek S.: Macromolecules 2000, 33,1964.

27. Duda A., Florjańczyk Z., Hofman A, Slomkowski S., Penczek 5.: Macromolecules 1990,23,1640.

28. Dolee T. J., Grates J. A.: "Acetal Resin" in: "Encyclopedia of Polymer Science and Engineering", Vol. 1. (Ed. Mark H. F. et al), New York, Chichester. Brisbane, Toronto, Singapore, Wiley-lnterscience, 1985, p.47 .

29. Duda A, Penczek S.: Macromolecules 1990, 23, 1636.

Google Scholar

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0

J. Libiszowski polimery@ichp.pl

Affiliation
Centre of Molecular and Macromolecular Studies, Polish Academy of Sciences, Department of Polymer Chemistry, ul. Sienkiewicza 112, 90-363 Łódź

A. Kowalski

Affiliation
Centre of Molecular and Macromolecular Studies, Polish Academy of Sciences, Department of Polymer Chemistry, ul. Sienkiewicza 112, 90-363 Łódź

T. Biela

Affiliation
Centre of Molecular and Macromolecular Studies, Polish Academy of Sciences, Department of Polymer Chemistry, ul. Sienkiewicza 112, 90-363 Łódź

A. Duda

Affiliation
Centre of Molecular and Macromolecular Studies, Polish Academy of Sciences, Department of Polymer Chemistry, ul. Sienkiewicza 112, 90-363 Łódź