Glass transition temperature-cure temperature-transformation (TgTT) diagram for EPY® epoxy system

M. Urbaniak

doi:10.14314/polimery.2018.1.3

Published : 2021-01-13

Vol. 63 No. 1 (2018)

Glass transition temperature-cure temperature-transformation (TgTT) diagram for EPY® epoxy system

M. Urbaniak

DOI: https://doi.org/10.14314/polimery.2018.1.3

Abstract

The EPY® epoxy system applied for the production of machine foundation chocks was isothermally cured at varying cure temperatures and times. The thermal behavior during the curing of the system was monitored by means of the glass transition temperature (Tg) and conversion degree (α) measured using differential scanning calorimetry (DSC) and rotational viscometry (ARES). Also, the thermal decomposition was measured by thermogravimetry and differential thermal analysis (TG-DTA). The results were analyzed and summarized in the generalized phase diagram, as well as in the Tg-cure temperature-transformation (TgTT) cure diagram. The phase diagram has reference to the transformations (in liquid, ungelled glass, gelled glass and rubber state) encountered at time to gelation and vitrification. Whereas the TgTT diagram shows that there are three types of behavior related to the temperature of cure and makes a useful framework for understanding and analyzing the relations and interdependencies during the curing process of the epoxy system.

Keywords

epoxy system ; curing ; gelation ; vitrification ; glass transition temperature ; glass transition temperature-cure temperature-transformation diagram układ epoksydowy ; sieciowanie ; żelowanie ; zeszklenie ; temperatura zeszklenia ; diagram temperatura zeszklenia-temperatura sieciowania-przemiana

Details

References

Statistics

Authors

Download files

PDF

Zasady cytowania

Urbaniak, M. (2021). Glass transition temperature-cure temperature-transformation (TgTT) diagram for EPY® epoxy system. Polimery, 63(1), 18-24. https://doi.org/10.14314/polimery.2018.1.3

References

Pascault J.P., Williams R.J.J.: “Epoxy Polymers. New Materials and Innovations”, Wiley-VCH, Weinheim 2010.

[2] Osswald T.A., Menges G.: “Material Science of Polymers for Engineers”, 3rd Ed., Hanser Verlag, Munich, Germany 2012.

[3] Baroncini E.A., Yadav S.K., Palmese G.R., Stanzione J.F.: Journal of Applied Polymer Science 2016, 133, 44 103.
Crossref

[4] Vergnaud J.-M., Bouzon J.: “Cure of Thermosetting Resins. Modelling and Experiments”, Springer-Verlag, London 1992.

[5] Wisanrakkit G., Gillham J.K., Enns J.B.: Journal of Applied Polymer Science 1990, 41, 1895.
Crossref

[6] Wisanrakkit G., Gillham J.K.: Journal of Applied Polymer Science 1990, 41, 2885.
Crossref

[7] Hale A., Macosko Ch.W., Bair H.E.: Macromolecules 1991, 24, 2610.
Crossref

[8] Pascault J.P., Williams R.J.J.: Journal of Polymer Science, Part B Polymer Physics 1990, 28, 85.
Crossref

[9] DiBenedetto A.T.: Journal of Polymer Science, Part B Polymer Physics 1987, 25, 1949.
Crossref

[10] Nielsen L.E.: Journal of Macromolecular Science, Part C Polymer Reviews 1969, C3, 69.
Crossref

[11] Ramis X., Cadenato A., Morancho J.M., Salla J.M.: Polymer 2003, 44, 2067.
Crossref

[12] Teil H., Page S.A., Michaud V., Manson J.-A.E.: Journal of Applied Polymer Science 2004, 93, 1774.
Crossref

[13] Marks M.J., Snelgrove R.V.: ACS Applied Materials and Interfaces 2009, 1, 921.
Crossref

[14] Pramanik M., Fowler E.W., Rawlins J.W.: Polymer Engineering and Science 2014, 54, 1990.
Crossref

[15] Urbaniak M.: Polimery 2011, 56, 240.

[16] Urbaniak M.: Polimery 2017, 62, 394.
Crossref

[17] Gillham J.K.: Polymer Engineering and Science 1986, 26, 1429.
Crossref

[18] Enns J.B., Gillham J.K.: Journal of Applied Polymer Science 1983, 28, 2567.
Crossref

[19] Simon S.L., Gillham J.K.: Journal of Applied Polymer Science 1994, 53, 709.
Crossref

[20] Adabbo H.E., Williams R.J.J.: Journal of Applied Polymer Science 1982, 27, 1327.
Crossref

[21] Urbaniak M., Grudziński K.: Polimery 2007, 52, 117.

[22] Urbaniak M., Grudziński K.: Polimery 2007, 52, 255.

[23] Wang X., Gillham J.K.: Journal of Applied Polymer Science 1993, 47, 425.
Crossref

[24] Gillham J.K., Enns J.B.: Trends in Polymer Science 1994, 2, 406.

[25] Urbaniak M.: Polimery 2008, 53, 537.

[26] Gillham J.K.: Polymer Engineering and Science 1979, 19, 676.
Crossref

[27] Gillham J.K., Benci J.A., Noshay A.: Journal of Applied Polymer Science 1974, 18, 951.
Crossref

[28] Grudziński K., Jaroszewicz W., Ratajczak J. et al.: “Mounting of machines and devices by using EPY resin compound”, ZAPOL Publisher, Szczecin 2015.

[29] Williams R.J.J.: “Transitions during network formation” in “Polymer Networks. Principles of their Formation, Structure and Properties” (Ed. Stepto R.F.T.), Blackie Acad. & Prof., London 1997, pp. 93–124.

[30] Ozawa T.: Journal of Thermal Analysis 1970, 2, 301.
Crossref

[31] Hohn A., Schumann M., Goetz L., Geiss P.L.: “AIP Conference Proceedings” 2016, 1779, 070003.
Crossref

[32] Williams R.J.J.: “Curing of Thermosets” in “Developments in Plastics Technology” (Eds. Whelan A., Craft J.L.), Elsevier Applied Science Publ., London 1985, vol. 2, pp. 339–379.

Google Scholar

Altmetric indicators

Citing articles via

CITEDBY SCOPUS

Statistics

Total abstract views : 139

PDF Downloads : 121