Katalizatory syntezy żywic winyloestrowych z epoksynowolaku i nienasyconego kwasu monokarboksylowego

G. Groszek; J. Maziopa

Published : 2022-09-01

Vol. 49 No. 11-12 (2004)

Catalysts of the synthesis of vinylester resins from epoxynovolac and unsaturated monocarboxylic acid

G. Groszek J. Maziopa

Abstract

Activities of four amine systems [based on commercial products - Formulae (I) - (IV)] catalyzing the addition of methacrylic acid to epoxy group of novolac have been compared. The necessity of use of two various catalysts during successive stages of the reaction have been found. Reactivity was determined on the basis of the measurements of changes of epoxy and acid numbers in course of reaction, final viscosity of the product and temperature profiles of the addition (Fig. 1 and 2, Table 1 and 2). The best catalytic system consists of 2,4,6-tris(N,N-dimethylaminomethyl) phenol (Ancamine K-54) as catalyst I and tetrabutylammonium bromide (TBABr) as catalyst II. The following properties of styrene solution of vinylester (VE) resin, prepared in the presence of this catalytic system, were characterized: reactivity, physicochemical properties before curing as well as functional properties after curing (Table 3).

Keywords

żywica winyloestrowa ; synteza ; katalizatory ; utwardzanie ; właściwości użytkowe vinylester resin ; synthesis ; catalysts ; curing ; functional properties

Similar Articles

B. Grabowska, M. Holtzer, Application of microwave radiation for crosslinking of sodium polyacrylate/silica gel system used as a binder in foundry sands , Polimery: Vol. 52 No. 11-12 (2007)
P. Czub, G. Kowalski, J. Pielichowski, Studies on the properties of epoxy-oxothiolane resins , Polimery: Vol. 45 No. 9 (2000)
A. Piegat, M. El Fray, Poly(ethylene terephthalate) modification with the monomer from renewable resources , Polimery: Vol. 52 No. 11-12 (2007)
B. Biernacki, Correlation of ralative elongation at break of cured resins with the resistance of resin-containing composites to low temperatures , Polimery: Vol. 45 No. 9 (2000)
I. Reksiak, G. Rokicki, Modified polyurethanes for biomedical applications , Polimery: Vol. 45 No. 9 (2000)
S. Łabużek, B. Nowak, J. Pająk, Biodegradation of aged composition of polyethylene with synthetic polyester , Polimery: Vol. 51 No. 1 (2006)
P. Obreja, F. Comanescu, M. Purica, R. Gavrila, D. Cristea, Polymers doped with metal oxide nanoparticles with controlled refractive index , Polimery: Vol. 52 No. 9 (2007)
A. Bukowska, W. Bukowski, H. Galina, A. Sztycharz, The kinetics of the reaction of methacrylic acid with Epidian 6 , Polimery: Vol. 45 No. 2 (2000)
A. Balas, M. Rajkiewicz, E. Grzywa, H. Janik, R. Lisowska, M. Gęsiak, E. Wojtyńska, D. Wilson-Polit, Dressing materials applied in orthopedic and traumatic injuries. Part II. Urethane quasiprepolymers as chemically reactive polyurethane—fabric composite dressing material components , Polimery: Vol. 46 No. 10 (2001)
Paweł Palutkiewicz, Tomasz Garbacz, Łukasz Hura, Influence of polymer flow rate, mold cavity volume and injection speed on selected properties of polypropylene molded parts , Polimery: Vol. 69 No. 7-8 (2024)

<< < 71 72 73 74 75 76 77 78 79 80 > >>

You may also start an advanced similarity search for this article.

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Groszek, G., & Maziopa, J. (2022). Catalysts of the synthesis of vinylester resins from epoxynovolac and unsaturated monocarboxylic acid. Polimery, 49(11-12), 780–784. Retrieved from https://ichp.vot.pl/index.php/p/article/view/1812

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0

G. Groszek ggroszek@prz.rzeszow.pl

Affiliation
Politechnika Rzeszowska, Katedra Technologii i Materiałoznawstwa Chemicznego, ul. W. Pola 2, 35-959 Rzeszów

J. Maziopa

Affiliation
Politechnika Rzeszowska, Katedra Technologii i Materiałoznawstwa Chemicznego, ul. W. Pola 2, 35-959 Rzeszów