Shape memory properties of poly(methyl methacrylate-co--2-hydroxyethyl methacrylate)/poly(ethylene glycol) complexes

G. Liu; D. Xie; Y. Li; Y. Zhang; F. Huang

Published : 2013-04-30

Vol. 58 No. 4 (2013)

Shape memory properties of poly(methyl methacrylate-co--2-hydroxyethyl methacrylate)/poly(ethylene glycol) complexes

G. Liu D. Xie Y. Li Y. Zhang F. Huang

Abstract

Poly(methyl methacrylate-co-2-hydroxyethyl methacrylate) [P(MMA-co-HEMA)] networks and linear poly(ethylene glycol) (PEG) can form complexes, which show shape memory properties due to a large difference in storage modulus (E') below and above its glass transition temperature (Tg). The morphology of prepared samples was analyzed using transmission electron microscopy (TEM) and X-ray diffraction (XRD) analysis. Differential scanning calorimetry (DSC) was used to investigate the thermal properties and dynamic mechanical analysis (DMA) to determine the effect of temperature on the mechanical properties. It was found that the shape recovery ratio could reach 98 %.

Keywords

poli(metakrylan metylu-co-metakrylan 2-hydroksyetylu) ; poli(glikol etylenowy) ; temperatura zeszklenia ; pamięć kształtu poly(methyl methacrylate-co-2-hydroxyethyl methacrylate) ; poly(ethylene glycol) ; glass transition temperature ; shape memory properties

Details

References

Statistics

Authors

Download files

PDF

Zasady cytowania

Liu, G., Xie, D., Li, Y., Zhang, Y., & Huang, F. (2013). Shape memory properties of poly(methyl methacrylate-co--2-hydroxyethyl methacrylate)/poly(ethylene glycol) complexes. Polimery, 58(4), 304-307. Retrieved from https://ichp.vot.pl/index.php/p/article/view/737

References

Lendlein A., Kelch S.: Angew. Chem. Int. Ed. 2002, 41, 2034.

2. Lendlein A., Langer R.: Science 2002, 296, 1673.

3. Samra B. K., Galaev I. Y., Mattiasson B.: Angew. Chem. Int. Ed. 2000, 39, 2364.

4. Hu Z., Zhang X., Li Y.: Science 1995, 269, 525.

5. Osada Y., Matsuda A.: Nature 1995, 376, 219.

6. Liu C., Qin H., Mather P. T.: J. Mater. Chem. 2007, 17, 1543.

7. Gunes I. S., Cao F., Jana S. C.: Polymer 2008, 49, 2223.

8. Yang B., Huang W. M., Li C., Li L.: Polymer 2006, 47, 1348.

9. Behl M., Lendlein A.: Mater. Today 2007, 10, 20.

10. Rousseau I. A., Mather P. T.: J. Am. Chem. Soc. 2003, 125, 15 300.

11. Liu C., Chun S. B., Mather P. T., Zheng L., Haley E. H., Coughlin E. B.: Macromolecules 2002, 35, 9868.

12. Lendlein A., Schmidt A. M., Langer R.: PNAS 2001, 98, 842.

13. Lee B. S., Chun B. C., Chung Y. C., Sul K. I., Cho J. W.: Macromolecules 2001, 34, 6431.

14. Liu C., Mather P. T.: Proceedings of the annual technical conference — society of plastics engineers, 61st, vol. 2. Brookfield, CT, USA: Society of Plastics Engineers 2003, pp. 1962—1966.

15. Behl M., Bellin I., Kelch S.,WagermaierW., Lendlein A.: Adv. Funct. Mater. 2009, 19, 102.

16. Grodzinski J. J.: Polym. Adv. Technol. 2010, 21, 27.

17. Tomić S. L., Micić M. M., Dobić S. N., Filipović J. M., Suljovrujić E. M.: Radiat. Phys. Chem. 2010, 79, 643.

18. Keller A.: J. Polym. Sci. 1959, 39, 151.

19. Kim B. K., Lee S. Y., Xu M.: Polymer 1996, 37, 5781.

Google Scholar

Citing articles via

Statistics

Total abstract views : 75

PDF Downloads : 58