Wpływ modyfikatorów na palność i właściwości fizyczne poliamidu 6

K. Kelar; B. Jurkowski; K. Mencel

Published : 2013-05-30

Vol. 58 No. 5 (2013)

Effect of modifiers on the flammability and physical properties of polyamide 6

K. Kelar B. Jurkowski K. Mencel

Abstract

Studies on the influence of selected modifiers (flame retardant, antioxidant, nanofiller) on the ignition, combustion and mechanical properties of polyamide 6 (PA 6) have been presented. The following methods were used: melt flow index (Table 2), oxygen index (Table 2), flammability UL-94 test (Table 2), thermogravimetric analysis (Fig. 2, Table 2) and strength characteristics in the static tensile test (Table 4). The smoke formation and heat release rate, the flammability of the material as well as the smoke density and toxicity of the volatile gas products released during the decomposition of the studied materials were determined using the cone calorimeter method under 35 kW/m2 heat flux conditions (Fig. 3, Table 3). It was found that the simultaneous use of three modifiers: 16 wt. % Exolite, 0.5 wt. % Irganox and 5 wt. % amine modified montmorillonite was most advantageous in terms of improving the fire safety of the materials.

Keywords

poliamid 6 ; antypiren ; montmorylonit ; palność ; właściwości mechaniczne polyamide 6 ; flame retardant ; montmorillonite ; flammability ; mechanical properties

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Kelar, K., Jurkowski, B., & Mencel, K. (2013). Effect of modifiers on the flammability and physical properties of polyamide 6. Polimery, 58(5), 365-370. Retrieved from https://ichp.vot.pl/index.php/p/article/view/742

References

Janowska G., Przygocki W., Włochowicz A.: „Palność polimerów i materiałów polimerowych”, WNT, Warszawa 2007.

2. Boryniec S., Przygocki W.: Polimery 1999, 44, 87.

3. Boryniec S., Przygocki W.: Polimery 1999, 44, 381.

4. Boryniec S., Przygocki W.: Polimery 1999, 44, 656.

5. Praca zbiorowa: „Materiały polimerowe o obniżonej palności” (red. Jurkowski B., Rydarowski H.), Wydawnictwo Naukowe Instytutu Technologii Eksploatacji — Państwowego Instytutu Badawczego, Radom 2012.

6. Jang B. N., Wilkie C. A.: Polymer 2005, 46, 3264.

7. Liu Y., Wang Q.: J. Polym. Res. 2009, 16, 583.

8. Liu H., Zhang W., Zheng S.: Polymer 2005, 46, 157.

9. Maspoch M. L., Fernando H. E., Velasco J. I.: Macromol. Symp. 2003, 194, 295.

10. Fornes T. D., Yoon P. J., Paul D. R.: Polymer 2003, 44, 754.

11. Li J., Tong L., Fang Z., Gu A., Xu Z.: Polym. Degrad. Stab. 2006, 91, 2046.

12. Feng J., Hao J., Du J., Yang R.: Polym. Degrad. Stab. 2012, 97, 605.

13. Półka M.: Polimery 2011, 56, 734.

14. Bourbigot S., Devaux E., Flambard X.: Polym. Degrad. Stab. 2002, 75, 397.

15. Konecki M., Półka M.: Polimery 2006, 51, 293.

16. Priya L., Jog J. P.: J. Polym. Sci., Part B 2003, 41, 31.

Google Scholar

Citing articles via

Statistics

Total abstract views : 133

PDF Downloads : 93