Temperature influence on volatile compounds emitted during thermo-oxidative degradation of poly(trimethylene terephthalate)

M. Dzięcioł

Published : 2012-02-28

Vol. 57 No. 2 (2012)

Temperature influence on volatile compounds emitted during thermo-oxidative degradation of poly(trimethylene terephthalate)

M. Dzięcioł

Abstract

The emission of volatile compounds formed during thermo-oxidative degradation of poly(trimethylene terephthalate) (PTT) was studied under isothermal conditions. The experiments were performed in a tubular furnace with a 0.025 m3/h air flow, at the temperatures of 200, 300, 400, 500, 600 and 700 °C. The weight loss of PTT and the amount of the solid degradation products were determined by gravimetric analysis. The volatile compounds were identified and quantified using gas chromatography and colorimetry methods. Analyses showed that the emitted volatiles are complex mixtures which consist of carbon oxides, aliphatic and aromatic hydrocarbons, aldehydes (including acrolein) and allyl alcohol. The temperature influence on the emission and composition of the volatile compounds evolved from PTT was discussed.

Keywords

poli(tereftalan trimetylenu) ; PTT ; poliestry ; rozkład termooksydacyjny ; destrukcja ; emisja lotnych związków poly(trimethylene terephthalate) ; PTT ; polyesters ; thermo-oxidative degradation ; decomposition ; volatile compounds emission

Details

References

Statistics

Authors

Download files

PDF

Zasady cytowania

Dzięcioł, M. (2012). Temperature influence on volatile compounds emitted during thermo-oxidative degradation of poly(trimethylene terephthalate). Polimery, 57(2), 106–110. Retrieved from https://ichp.vot.pl/index.php/p/article/view/811

References

Schultz J. M., Wu J. in: "Handbook of Thermoplastic Polyesters", Wiley, Weinheim 2002, Chap.12, p. 551--578.

2. Chuah H. H.: Chem. Fiber Int. 1996, 46, 424.

3. Pyda M., Boller A., Grebowicz J., Chuah H., Lebedev B. V., Wunderlich B.: J. Polym. Sci., Part B: Polym. Phys. 1998, 36, 2499.

4. Chung W.-T., Yeh W.-J., Hong P.-D.: J. Appl. Polym. Sci. 2002, 83, 2426.

5. Ramiro J., Eguiazábal J. I., Nazabál J.: J. Appl. Polym. Sci. 2002, 86, 2775.

6. Wu G., Li H., Wu Y., Cuculo J. A.: Polymer 2002, 43, 4915.

7. Zhang J.: J. Appl. Polym. Sci. 2004, 91, 1657.

8. Srimoaon P., Dangseeyun N., Supaphol P.: Eur. Polym. J. 2004, 40, 599.

9. Chen K., Shen J., Tang X.: J. Appl. Polym. Sci. 2005, 97, 705.

10. Wang X.-S., Li X.-G., Yan D.: Polym. Test. 2001, 20, 491.

11. Wang X.-S., Li X.-G., Yan D.: J. Appl. Polym. Sci. 2002, 84, 1600.

12. Kelsey D. R., Kiibler K. S., Tutunjian P. N.: Polymer 2005, 46, 8937.

13. Al-Mulla A., Shaban H. I.: Int. J. Polym. Mater. 2008, 57, 275.

14. Liu J., Bian S. G., Xiao M., Wang S. J., Meng Y. Z.: Chinese Chem. Lett. 2009, 20, 487.

15. Wang X.-S., Li X.-G., Yan D.: Polym. Degrad. Stab. 2000, 69, 361.

16. Fairgrieve S. F.: "Degradation and Stabilisation of Aromatic Polyesters", Smithers Rapra Technology, 2009.

17. Stec A., Hull R.: "Fire Toxicity and its Assessment" in: "Fire Retardancy of Polymeric Materials" (Ed. Wilkie C. A., Morgan A. B.), CRC Press Boca Raton 2009, Chap.17, p. 453--477.

18. Dzięcioł M., Trzeszczyński J.: J. Appl. Polym. Sci. 1998, 69, 2377.

19. Dzięcioł M.: Int. J. Environ. Anal. Chem. 2009, 89, 881.

Google Scholar

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0