Nanokompozyty poliwęglanouretanowe z nanokrzemionką do zastosowań na implanty krążka międzykręgowego

B. Waśniewski; M. Auguścik; P. Parzuchowski; M. Zielecka; J. Ryszkowska

Published : 2012-12-30

Vol. 57 No. 11-12 (2012)

Polycarbonate urethane nanocomposites with nanosilica for implants of the intervertebral disc

B. Waśniewski M. Auguścik P. Parzuchowski M. Zielecka J. Ryszkowska

Abstract

Two types of nanocomposites with polycarbonate urethane (PUR) matrix were made in order to obtain an elastic material intended for the implant of intervertebral disc. Oligocarbonate diols of different molar masses (1534 g/mol and 1750 g/mol) were used for the synthesis. Each of the composites contained 0.5 wt. % silica with an average nanoparticle size of 57 nm. The produced materials were characterized for strength properties and investigated by thermogravimetric analysis (TGA), differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA). The chemical structure of the produced nanocomposites was confirmed on the basis of Fourier transform infrared spectroscopy (FT-IR), while the adhesive properties were evaluated by contact angle measurements.

Keywords

poliwęglanouretany ; nanokrzemionka ; nanokompozyty ; implant ; krążek międzykręgowy polycarbonate urethanes ; nanosilica ; nanocomposites ; implant ; intervertebral disc

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Waśniewski, B., Auguścik, M., Parzuchowski, P., Zielecka, M., & Ryszkowska, J. (2012). Polycarbonate urethane nanocomposites with nanosilica for implants of the intervertebral disc. Polimery, 57(11-12), 812-818. Retrieved from https://ichp.vot.pl/index.php/p/article/view/877

References

Winters J. M., Herkowitz H. N.: ArgoSpine News J. 2011, 23, 3.

2. Barrey Cedric Y.: ArgoSpine News J. 2009, 21, 78.

3. Taksali S., Grauer J. N., Vaccaro A. R.: The Spine Journal 2004, 4, 231.

4. Janik H.: Polimery 2010, 55, 421.

5. Wang Y. T., Chang T. C., Hong Y. S., Chen H. B.: Thermochim. Acta 2003, 397, 219.

6. Shang X. Y., Zhu Z. K., Yin J., Ma X. D.: Chem. Mater. 2002, 14, 71.

7. Matejka L., Duek K., Pleštil J., Kríz J., Lednický F.: Polymer 1999, 40, 171.

8. Huang Z. H., Qiu K. Y.: Polymer 1997, 38, 521.

9. Yu Y. Y., Chen C. Y., Chen W. C.: Polymer 2003, 44, 593.

10. Zhou S. X., Wu L. M., Sun J., Shen W. D.: Prog. Org. Coat. 2002, 45, 33.

11. Pu Z. C., Mark J. E.: Chem. Mater. 1997, 9, 2442.

12. Chen Y., Iroh J. O.: Chem. Mater. 1999, 11, 1218.

13. Ryszkowska J., Waoeniewski B., Pytel A., Zielecka M.: Polimery 2009, 54, 657.

14. Nerurkar N., Dawn E., Mauck R.: J. Biomech. 2010, 43, 1017.

15. Yan C., Jude O. I.: Chem. Mater. 1999, 11, 1218.

16. Wang Y. T., Chang T. C., Hong Y. S., Chen H. B.: Thermochim. Acta 2003, 397, 219.

17. Ogoshi T., Itoh H., Kim K. M., Chujo Y.: Macromolecules 2002, 35, 334.

18. Vega-Baudrit J., Sibaja-Ballestero M., Vazquez P., Torregrosa-Macia R., M.-Martinez J. M.: Inter. J. Adhes. Adhes. 2007, 27, 469.

19. Yeh F., Yeh F., Hsiao B. S., Sauer B. S., Michel S., Siesler H.W.: Macromolecules 2003, 36, 1940.

20. Ryszkowska J.: „Rola budowy chemicznej i warunków procesu wytwarzania w kształtowaniu morfologii oraz właściwości materiałów poliuretanowych”, Oficyna Wydawnicza Politechniki Warszawskiej, Warszawa 2011.

21. Hepburn C.: „Polyurethane Elastomers”, Elsevier Science Publishers LTD, New York 1992.

22. Sobolewska E., Frączek B., Błażewicz S., Seńko K., Lipski M.: Protet. Stomatol. 2009, LIX (6), 401.

23. Gonzalez-Martin L. M., Labajos-Broncano L., Jańczuk B., Broque J. M.: J. Mater. Sci. 1999, 34, 5923.

24. Żenkiewicz M.: Polimery 2005, 50, 365.

25. Hutchinson A. R., Iglauer S.: Int. J. Adhes. Adhes. 2006, 26, 555.

26. Della Volpe C., Siboni S.: J. Colloid. Interface Sci. 1997, 195, 121.

27. Garbacz T.: Polimery 2004, 49, 23.

28. Rudawska A.: Polimery 2008, 53, 452

Google Scholar

Citing articles via

Statistics

Total abstract views : 74

PDF Downloads : 101

B. Waśniewski polimery@ichp.pl

M. Auguścik

P. Parzuchowski

M. Zielecka

J. Ryszkowska