Włókna konopne modyfikowane chemicznie przeznaczone do wzmacniania polimerów

J. W. Kaczmar; J. Pach; C. Burgstaller

Published : 2011-12-30

Vol. 56 No. 11-12 (2011)

The chemically treated hemp fibres to reinforce polymers

J. W. Kaczmar J. Pach C. Burgstaller

Abstract

The effect of different chemical treatments of hemp fibres, carried out by alkali treatment, acetylation and modification with maleic anhydride, on their physical, thermal and chemical properties as well as their surface characteristic was discussed in this paper. The morphology of the fibres was investigated by SEM. Thermal properties were investigated by TGA and DTA methods and the chemical composition of fibres by FT-IR spectroscopy. Chemical modifications resulted in the lowered content of lignin, pectin and hemicellulose, what is especially observable with mercerised fibres. Another effect of the chemical treatment applied is related to the removal of waxy substances from the surface, which was indirectly ascertained by SEM observation, which revealed a relatively smooth hemp fibres surface. TGA results showed that the applied chemical fibre treatment resulted in the lowered thermal degradation of the treated fibres, after the removal of non-cellulose components, especially lignin.

Keywords

włókna konopne ; modyfikacja chemiczna ; alkalizacja ; acetylowanie hemp fibres ; chemical treatment ; alkali treatment ; acetylation

Details

References

Statistics

Authors

Download files

PDF

Zasady cytowania

Kaczmar, J. W., Pach, J., & Burgstaller, C. (2011). The chemically treated hemp fibres to reinforce polymers. Polimery, 56(11-12), 817-822. Retrieved from https://ichp.vot.pl/index.php/p/article/view/971

References

Bledzki A. K., Gassan J.: Prog. Polym. Sci. 1999, 24, 221.

2. Bos H. K., Müssig J., van den Oever M.: Composites Part A 2006, 37, 1591.

3. Tserki V., Zafeiropoulos N. E., Simon F., Panayiotou C.: Composites Part A 2005, 36, 1110.

4. Abdel-Nasser A., El-Hendawy: J. Anal. Appl. Pyrolysis 2006, 75, 159.

5. Kaczmar J. W., Pach J., Kozłowski R.: Polimery 2006, 51, 722.

6. Herrera-Franco P. J., Valadez-Gonzalez A.: Composites Part B, 2005, 36, 597.

7. Steller R., Meissner W.: Polimery 2002, 47, 332.

8. Ke G., Yu W., Xu W., Cui W., Shen X.: J. Mater. Process. Technol. 2008, 207, 125.

9. Sakata I., Morita M., Tsuruta N., Morita K.: J. Appl. Polym. Sci. 1993, 49, 1251.

10. Wang Q., Kaliaguine S., Ait-Kadi A.: J. Appl. Polym. Sci. 1993, 48, 121.

11. Li X., Tabil L. G., Oguocha I. N., Panigrahi S.: Compos. Sci. Technol. 2008, 68, 1753.

12. Bledzki A., Faruk O.: Appl. Compos. Mater. 2003, 10, 365.

13. Ghosh P., Dev D., Samanta A. K.: J. Appl. Polym. Sci. 1998, 68, 1139.

14. Gomex-Bueso J., Westin M., Torgilsson R., Olesen P. O., Simonson R.: Holz Roh Werkst. 1999, 57, 178.

15. Joseph K., Thomas S., Pavithan C.: Polymer 1996, 37, 5131.

16. Cantero G., Arbelaiz A., Llano-Ponte R., Mondragon I.: Compos. Sci. Technol. 2003, 63, 1247.

17. Chang S. T., Chang H. T.: Polym. Degrad. Stabil. 2001, 71, 261.

18. Colom X., Carrillo F., Nogues F., Garriga P.: Polym. Degrad. Stabil. 2003, 80, 543.

19. Sgriccia N., Hawley M. C., Misra M.: Composites Part A 2008, 39, 1632.

20. Kostic M., Pejic B., Scundric P.: Bioresour. Technol. 2008, 99, 94.

21. Wang H. M., Postle R., Kessler R., Kessler W.: Text. Res. J. 2003, 73, 664.

22. Ouajai S., Shanks R. A.: Polym. Degrad. Stabil. 2005, 89, 327.

23. Pach J., Kaczmar J.: Polimery 2011, 56, 385.

Google Scholar

Citing articles via

Statistics

Total abstract views : 99

PDF Downloads : 52