Coating materials obtained from polyurethane cationomers modified with functionalized silsequioxanes. Part II. Practical properties

B. Król P. Król

Abstract

Studies on the physicochemical properties and applications of polymer coatings obtained from the dispersion of aqueous polyurethane cationomers modified with silsequioxanes functionalized with OH groups [(PHIPOSS) (Table 1)] have been presented. The obtained cationomers has been classified as possessing a nanocomposite structure and high, increasing with PHIPOSS content, thermostability (Fig. 1, Table 3). The coatings were studied with special emphasis on determining the influence of PHIPOSS on the interactions occurring in the rigid polyurethane-urea segments, on which the morphology of the obtained surfaces depend. The morphology was evaluated by microscopic analysis methods (Fig. 3,4, Table 5) and DSC (Fig. 2, Table 4). The surface energy (Table 2,6) and applicability of the coatings were also determined (Table 7). Preliminary studies indicate potential for application of the products obtained in the form of presented aqueous dispersions as environmentally friendly coatings on surfaces of hydrophilic character.

Keywords

powłoki ochronne ; nanokompozyt ; kationomer poliuretanowy ; funkcjonalizowany silseskwioksan (POSS) ; charakterystyka powierzchni ; właściwości użytkowe protective coatings ; nanocomposite ; polyurethane cationomer ; functionalized silsequioxanes (POSS) ; surface characteristics ; applicability

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Król, B., & Król, P. (2010). Coating materials obtained from polyurethane cationomers modified with functionalized silsequioxanes. Part II. Practical properties. Polimery, 55(11-12), 855-862. Retrieved from https://ichp.vot.pl/index.php/p/article/view/1075

References

Król B., Król P.: Polimery 2010, 55, 440.

2. Madhavan K., Reddy B. S. R.: J. Appl. Polym. Sci. 2009, 113, 4052.

3. Madhavan K., Gnanasekaran D., Reddy B. S. R.: J. Appl. Polym. Sci. 2009, 114, 3659.

4. Chattopadhyay D. K., Webster D. C.: Prog. Polym. Sci. 2009, 34, 1068.

5. Bourbigot S., Turf Y., Bellayer S., Duquesne S.: Polymer Degrad. Stability 2009, 94, 1230.

6. Lai Y. S., Tsai C. W, Yang H. W, Wang G. R, Wu K. H.: Mat. Chem. & Phys. 2009, 117, 834.

7. Raghunath J., Gergiou G., Armitage D., Nazhat S. M., Sales K. M., Butler P. E., Seifalian A. M.: J. Biomed. Mater. 2008, 91A, 834.

8. Good J. R.: „Fundamentals of Adhesion” (red. Lee L. H.), Dekker, New York 1991, str. 153.

9. Żenkiewicz M.: „Modyfikowanie warstwy wierzchniej tworzyw wielkocząsteczkowych”, WNT, Warszawa 2000.

10. van Oss C. J.: Chem. Rev. 1988, 88, 927.

11. ZismanW. A.:Adv. Chem. (wyd.Am. Chem. Soc.) 1964, 43, 1.

12. Pat. USA 6 362 279 (2002).

13. Janowski B., Pielichowski K.: Polimery 2008, 53, 87.

14. Król R, Król B.: Colloid Polym. Sci. 2009, 287, 189.

15. Król R, Król B.: Polimery 2007, 52, 427.

16. Król R, Byczyński Ł.: Przem. Chem. 2007, 86, 643.

Google Scholar

Citing articles via

Statistics

Total abstract views : 54

PDF Downloads : 17