Relationship between fracture toughness and temperature in epoxy coatings

Z. Bo; L. Jing-wei; L. Shu-guang; L. Yi-hui; H. Ju-tao

doi:10.14314/polimery.2015.258

Published : 2015-04-30

Vol. 60 No. 4 (2015)

Relationship between fracture toughness and temperature in epoxy coatings

Z. Bo L. Jing-wei L. Shu-guang L. Yi-hui H. Ju-tao

DOI: https://doi.org/10.14314/polimery.2015.258

Abstract

The fracture toughness KIC of nine kinds of epoxy coating specimens was tested in the temperature range from 20 to -40 °C, and the influence of temperature on KIC was discussed. The results showed that KIC decreases sharply in unmodified systems but increases for some specimens with 20—50 portions of rubber impact modifier. The elastic modulus test indicated that KIC is closely related with the modulus. Scanning Electron Microscopy images showed that the introduction of impact modifier to epoxy can enlarge the ductile deformation of the fracture surface. As a result, the addition of rubber modifier is a suitable path to improve the anti-cracking performance of epoxy coatings at low temperature due to an increase of fracture toughness and reduction of elastic modulus, which thus can reduce the thermal stress in the process of cooling.

Keywords

epoxy resin ; fracture toughness żywica epoksydowa ; kruche pękanie

Details

References

Statistics

Authors

Download files

PDF

Zasady cytowania

Bo, Z., Jing-wei, L., Shu-guang, L., Yi-hui, L., & Ju-tao, H. (2015). Relationship between fracture toughness and temperature in epoxy coatings. Polimery, 60(4), 258–263. https://doi.org/10.14314/polimery.2015.258

References

McGarry F.J.: Proceedings of the Royal Society of London, Series A 1970, 319, 59. http://dx.doi.org/10.1098/rspa.1970.0165

[2] Hedrick J.L., Yilgor I., Wilkes G.L., McGrath J.E.: Polymer Bulletin 1985, 13, 201.

[3] Kim S.C., Brown H.R.: Journal of Materials Science 1987, 22, 2589.

[4] Paul D.R, Bucknall C.B.: “Polymer Blends: Formulation & Performance”. The Science Press, Beijing 2004 (in Chinese), p. 630.

[5] Deng S., Ye L., Friedrich K.: Journal of Materials Science 2007, 42, 2766. http://dx.doi.org/10.1007/s10853-006-1420-x

[6] Kwon S.-C., Adachi T., Araki W.: Composites, Part B 2008, 39, 773, http://dx.doi.org/10.1016/j.compositesb.2007.10.008

[7] Tomiæ M.D., Dunjiæ B., Likiæ V. et al.: Progress in organic coatings 2014, 77, 518. http://dx.doi.org/10.1016/j.progcoat.2013.11.017

[8] Paul D.R., Bucknall C.B.: “Polymer Blends: Formulation& Performance”, The Science Press, Beijing 2004 (in Chinese), p. 602.

[9] Li Z.-h., Chou J.-n., Deng F.-y.: Guangzhou Chemistry 2007, 32 (2), 73.

Google Scholar

Altmetric indicators

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0

Z. Bo zhaobo@iwhr.com

Affiliation
China Institute of Water Resources and Hydropower Research, State Key Laboratory of Simulation and Regulation of Water Cycle in River Basin, Beijing, 100038, China

L. Jing-wei

Affiliation
China Institute of Water Resources and Hydropower Research, State Key Laboratory of Simulation and Regulation of Water Cycle in River Basin, Beijing, 100038, China

L. Shu-guang

Affiliation
China Institute of Water Resources and Hydropower Research, State Key Laboratory of Simulation and Regulation of Water Cycle in River Basin, Beijing, 100038, China

L. Yi-hui

Affiliation
China Institute of Water Resources and Hydropower Research, State Key Laboratory of Simulation and Regulation of Water Cycle in River Basin, Beijing, 100038, China

H. Ju-tao

Affiliation
China Institute of Water Resources and Hydropower Research, State Key Laboratory of Simulation and Regulation of Water Cycle in River Basin, Beijing, 100038, China