Synthesis of poly(L-lactic-co-glycolic acid) telechelic prepolymers by direct melt polycondensation, and their characterization

P. P. Sobecki; R. Ukielski

Published : 2022-08-30

Vol. 51 No. 7-8 (2006)

Synthesis of poly(L-lactic-co-glycolic acid) telechelic prepolymers by direct melt polycondensation, and their characterization

P. P. Sobecki R. Ukielski

Abstract

A series of L-lactic/glycolic acid polymers (PLLGAc) differing in molar ratios of L-lactic (L-LAc) to glycolic (GAc) acid and of relatively low molecular weights [Mn(theor) = 4000] were synthesized by direct melt polycondensation in the presence of 1,4-butanediol and sulfuric acid as a molecular weight regulator and catalyst, respectively. The characterization experiments (FT-IR, 1H NMR) demonstrated a good correlation between the polymer compositions and the ratios of L-LAc and GAc in the feed. The DSC studies of the prepolymers indicated that the melting point as well as degree of crystallinity of PLLGAc decreased with the increase in the molar fraction of GA units in the copolymer. The glass transition temperatures of the polymers varied from 29 to 45 C degrees, depending on the polymer composition. The alkaline hydrolyzability (0.1 M NaOH, 37 C degrees) of the polymers is strongly affected by GA content in PLLGAc. With increasing GA content in the prepolymer, weight loss of a sample becomes faster.

Keywords

kwas mlekowy ; kwas glikolowy ; prepolimer ; polikondensacja lactic acid ; glycolic acid ; prepolymer ; polycondensation

Details

References

Statistics

Authors

Download files

PDF

Zasady cytowania

Sobecki, P. P., & Ukielski, R. (2022). Synthesis of poly(L-lactic-co-glycolic acid) telechelic prepolymers by direct melt polycondensation, and their characterization. Polimery, 51(7-8), 588–593. Retrieved from https://ichp.vot.pl/index.php/p/article/view/1561

References

Perrin D. E., English J. R: "Polyglycolide and Polylactide" in "Handbook of Biodegradable Polymers" (ed. Domb A. J., Kost J., Wiseman D. M.), Harwood Academic Publishers, Amsterdam 1997, pp. 3—27.

2. Gogolewski S.: Injury 2000, 31,28.

3. Dechy-Cabaret O., Martin-Vaca B., Bourissou D.: Chem. Rev. 2004,104, 6147.

4. Duda A., Penczek S.: Polimery 2003, 48,16.

5. Kricheldorf H. R., Kreiser-Saunders L, Damrau D.-O.: Macromol Symp. 2000,159,247.

6. Moon S. L, Lee C. W., Miyamoto M., Kimura Y.: J. Polym. Sci., Part A: Polym. Chem. 2000, 38,1673.

7. Takahashi K., Taniguchi L, Miyamoto M., Kimura Y: Polymer 2000, 41, 8725.

8. Moon S. L, Deguchi K., Miyamoto M., Kimura Y: Polym. Int. 2004, 53,254.

9. Gao Q. W., Lan P, Shao H. L., Hu X. C.: Polym. J. 2002, 34, 786.

10. Hiltunen K., Seppala J. V.: J. Appl Polym. Sci. 1998,67, 1017.

11. Hiltunen K., Seppala J. V., Harkónen M.: Macromolecules 1997, 30, 373.

12. Hiltunen K., Harkónen M., Seppala J. Yaananen T., V: Macromolecules 1996, 29, 8677.

13. Kylma J., Tuominen J., Helminen A., Seppala J. V.: Polymer 2001, 42, 3333.

14. Libiszowski J., Kowalski A., Biela T., Duda A.: Polimery 2004,49, 690.

15. Wang Z.-Y, Zhao Y.-M., Wang R, Wang J.: J. Appl Polym. Sci. 2006, 99, 244.

16. Ajioka M., Enomoto K., Suzuki K., Yamaguchi A.: J. Environ. Polym. Degrad. 1995, 3, 225.

17. Stolt M., Hiltunen K., Sódergard A.: Biomacromoecules 200l,2,1243.

18. Nederberg R, Connor E. E, Móller M., Glauser T., Hedrick J. L.: Angew. Chem., Int. Ed. 2001,40,2712.

19. Myers M., Connor E. E, Glauser T., Mock A., Nyce G., Hedrick J. L.: J. Pol. Sci, Part A: Polym. Chem. 2002, 40, 844.

20. Connor E. E, Nyce G. W., Myers M., Mock A., Hedrick J. L.: J. Am. Chem. Soc. 2002,124, 914.

21. Bourissou, D., Martin-Vaca, B., Dumitrescu, A., Graullier, M., Lacombe, E: Macromolecules 2005, 38, 9993.

22. Gilding D. K., Reed A. M.: Polymer 1979,20,1459.

23. Pat. USA 6313319(2001).

24. Duda A.:Polimery 2002,47,476.

25. Miyata T., Masuko T.: Polymer 1998,39,5515.

26. Kasperczyk J,: Polymer 1996,37,201.

27. Li S., Garreau H., Vert M.: J. Mater. Sci., Mater. Med. 1990,1,131.

28. Tsuji H., Tezuka Y.: Macromol Biosci. 2005, 5,135.

Google Scholar

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0