Otrzymywanie i właściwości elastomerowych silikonowych warstw antyadhezyjnych na papierze i pergaminie

J. Chruściel; T. Graczyk

Published : 2022-08-30

Vol. 51 No. 3 (2006)

Preparation and properties of elastomeric silicone anti- -adhesion layers on a paper or parchment

J. Chruściel T. Graczyk

Abstract

Hydrolytic polycondensation and catalytic equilibration methods were used for preparation of poly(dimethyl-co-methylvinyl)siloxanes (PMVS) Me3SiO(Me2SiO)m(MeViSiO)nSiMe3 and poly(dimethyl-co-methylhydro)siloxanes (PMHS) Me3Si(Me2SiO)k(MeHSiO)lSiMe3 differing in molecular weights so also in m and n values as well as k and l (Table 1-3). As a result of crosslinking of PMVS with PMHS, with use of commercial platinic catalysts (Table 4), thin layers of silicone elastomers on a paper or parchment were obtained. In the same way the comparative coatings of commercial silicones were prepared with use of catalysts produced by three leader companies (Table 5). The following properties of the coatings were investigated: basis weight, abrasion, migration of the components at room temperature and at temp. 70 oC and release force (showing the release properties) (Table 6 and 7). The coatings made of silicone elastomers prepared in our syntheses showed similar properties to the layers made of commercial products.

Keywords

silikonowe powłoki antyadhezyjne ; właściwości użytkowe ; elastomery silikonowe ; poli(dimetylo-co-metylowinylo)siloksany ; poli(dimetylo-co-metylowodoro)siloksany silicone release coatings ; functional properties ; silicone elastomers ; poly(dimethyl-co-methylvinyl)siloxanes ; poly(dimethyl-co-methylhydro)siloxanes

Details

References

Statistics

Authors

Download files

PDF (Język Polski)

Zasady cytowania

Chruściel, J., & Graczyk, T. (2022). Preparation and properties of elastomeric silicone anti- -adhesion layers on a paper or parchment. Polimery, 51(3), 192–198. Retrieved from https://ichp.vot.pl/index.php/p/article/view/1514

References

Chruściel J.: Polimery 1999, 44,586.

2. Kobayashi K., Takimoto S., Osawa Z.: Polym. Buli. 1998, 41, 77, i odnośniki tamże.

3. Brook M. A.: „Silicon in Organie, Organometallic and Polymer Chemistry", J. Wiley & Sons, Nowy Jork—Chichester—Weinheim—Brisbane—Singapur —Toronto 2000, i odnośniki tamże.

4. Stein J., Grade H., Williams E. A., Codella P. J., Smith J. E: J. Appl Polym. Sci. 1993,47,2257.

5. De Buyl E: Int. J. Adh. 2001,21,411.

6. Rościszewski R, Zielecka M.: „Silikony — właściwości i zastosowanie", WNT, Warszawa 2002.

7. Pat. jap. 2000 160 101 (2000); wg CA 2000,133,18881.

8. Czech Z., Gorący K.: Polimery 2005, 50, 762.

9. Zielecka M.: Polimery 2004,49,327.

10. Inoue H., Matsumoto A., Matsukawa K., Ueda A., Nagai S.:J. Appl. Polym. Sci. 1990, 40,1917.

11. Inoue H., Matsumoto A., Matsukawa K., Ueda A., Nagai S.: J. Appl. Polym. Sci. 1991,41,1815.

12. Dwight D. W., McGrath J. E., Riffle J. S., Smith S. D., York G. A.: J. Electron Spect. 1990, 52,457.

13. Tezuka Y., Ono T., Imai K.: J. Colloid Interf. 1990,136, 408.

14. Tezuka Y, Ono T., Imai K.: J. Chem. Soc., Faraday Trans. 1991,87,147.

15. He X. W., Widmaier J. M., Herz J. E., Meyer G. C.: Polymer l992,33,866.

16. Bischoff R., Cray S. E.: Próg. Polym. Sci. 1999,24,185.

17. a) Owen M. J.: „Siloxane Surface Activity" w „Silicon-Based Polymer Science: A Comprehensive Resource" (red. Zeigler J. M., Fearon M. W. G.), American Chem. Soc. Adv. Chem. Ser. 224, Washington DC, 1990; b) Owen M. J.: „Surface Chemistry and Applications" w „Siloxane Polymers" (red. Clarson S. J., Semlyen J. A.), Prentice Hali, 1993.

18. Noll W.: „Chemistry and Technology of Silicones", Academic Press, Nowy Jork 1968.

19. Owen M. J.: Chemtech 1981,11,288.

20. Marciniec B., Guliński J., Urbaniak W., Kornetka Z. W.: „Comprehensive Handbook on Hydrosilylation" (red. Marciniec B.), Pergammon Press, Oxford— Nowy Jork—Seul—Tokio 1992.

21. a) Chandra G., Lo P. Y, Hitchcock P. B., Lappert M. E: Organometallics 1987,6,191; b) Warhurst J. W., Hitchcock P. B., Lappert M. E, Warhurst J. W.: Angew. Chem., Int. Ed. Engl. 1991, 30,438.

22. Pat. europ. 980 903 (2000); wg CA 2000,132,167 723.

23. Pat. franc. 2 773 166 (1999); wg CA 2000,132,50 685.

24. Pat. jap. 11 349 774 (1999); wg CA 2000,132, 50 655.

25. Kreshkov A., Bork V. A., Shvyrkova L. A.: Zavod. Lab. 1962,28,151.

Google Scholar

Citing articles via

Statistics

Total abstract views : 0

PDF Downloads : 0